Compounds of poly(ionic liquid)s (PILs), derived from imidazole with different alkylic chain lengths located in the third position of the imidazolium ring (poly(1-vinyl-3-dodecyl-imidazolium) (PImC₁₂), poly(1-vinyl-3-octylimidazolium) (PImC₈) and poly(1-vinyl-3-butylimidazolium) (PImC₄) hexafluorophosphate) were synthesized. These compounds were tested as corrosion inhibitors on aluminum alloy AA6061 in diluted sulfuric acid (0.1–1 M H₂SO₄) by weight loss tests, polarization resistance measurements and inductively coupled plasma optical emission spectroscopy. Langmuir’s isotherms suggested film formation on bare alloy while standard free energy indicated inhibition by a physisorption process. However, compound efficiencies as inhibitors ranked low (PImC₁₂ > PImC₈ > PImC₄) to reach 61% for PImC₁₂ in highly diluted acidic solution. Apparently, the high mobility of sulfates favored their adsorption in comparison to PILs. The surface film displayed general corrosion, and pitting occurred as a consequence of PILs’ partial inhibition along with a continuous dissolution of defective patchy film on formation. A slight improvement in efficiency was displayed by compounds having high molecular weight and a long alkyl chain, as a consequence of steric hindrance and PIL interactions.

The effect of weld passes and single V grove designs on the corrosion resistance of dissimilar welds of a low alloy steel and a super duplex stainless steel was studied in synthetic brine. Welds were manufactured in argon by the gas tungsten arc technique and joined by a high nickel wire of super duplex stainless steel. Samples of weld regions were characterized by composition scans, electrochemical measurements, microhardness, and scanning electron microscopy. In X52/ER2594, a transition region of grain boundaries type II and a band of martensite were formed. The base metal of X52 underwent the highest corrosion rate and localized corrosion occurred in the heat affected zone. Interface ER2594/25Cr7Ni and 25Cr7Ni showed the presence of pitting near intermetallics.