Chromium (Cr)-doped cobalt ferrite nanoparticles were synthesized using a sol–gel autocombustion method, with the chemical formula CoCr_xFe_2xO₄. The value of x ranged from 0.00 to 0.5 in 0.1 increments. X-ray diffraction analysis confirmed the development of highly crystalline cubic spinel structures for all samples, with an average crystallite size of approximately 40 to 45 nm determined using the Scherrer equation. Pellets were prepared using a traditional ceramic method. The magnetic and magnetostrictive properties of the samples were tested using strain gauge and VSM (vibrating sample magnetometer) techniques. The results of the magnetic and magnetostrictive tests showed that the chromium-substituted cobalt ferrites exhibited higher strain derivative magnitudes than pure cobalt ferrite. These findings indicated that the introduction of chromium into the cobalt ferrite structure led to changes in the material’s magnetic properties. These changes were attributed to anisotropic contributions, resulting from an increased presence of Co²⁺ ions at B-sites due to the chromium substitutions. In summary, this study concluded that introducing chromium into the cobalt ferrite structure caused alterations in the material’s magnetic properties, which were explained by changes in the cationic arrangement within the crystal lattice. This study successfully explained these alterations using magnetization and coercivity data and the probable cationic dispersion.

This study generally relates to nuclear sensors and specifically to detecting nuclear and electromagnetic radiation using an ultrasensitive quartz tuning fork (QTF) sensor. We aim to detect low doses of gamma radiation with fast response time using QTF. Three different types of QTFs (uncoated and gold coated) were used in this study in order to investigate their sensitivity to gamma radiations. Our results show that a thick gold coating on QTF can enhance the quality factor and increase the resonance frequency from 32.7 to 32.9 kHz as compared to uncoated QTF. The results also show that increasing the surface area of the gold coating on the QTF can significantly enhance the sensitivity of the QTF to radiation. We investigated the properties of gold-coated and uncoated QTFs before and after irradiation by scanning electron microscopy. We further investigated the optical properties of SiO₂ wafers (quartz) by spectroscopic ellipsometry (SE). The SE studies revealed that even a small change in the microstructure of the material caused by gamma radiation would have an impact on mechanical properties of QTF, resulting in a shift in resonance frequency. Overall, the results of the experiments demonstrated the feasibility of using QTF sensors as an easy to use, low-cost, and sensitive radiation detector.