Rapid population and economic growth, excessive use of fossil fuels, and climate change have contributed to a serious turn towards environmental management and sustainability. The agricultural sector is a big contributor to (lignocellulosic) waste, which accumulates in landfills and ultimately gets burned, polluting the environment. In response to the current climate-change crisis, policymakers and researchers are, respectively, encouraging and seeking ways of creating value-added products from generated waste. Recently, agricultural waste has been regularly appearing in articles communicating the production of a range of carbon and polymeric materials worldwide. The extraction of cellulose nanocrystals (CNCs) and carbon quantum dots (CQDs) from biomass waste partially occupies some of the waste-recycling and management space. Further, the new materials generated from this waste promise to be effective and competitive in emerging markets. This short review summarizes recent work in the area of CNCs and CQDs synthesised from biomass waste. Synthesis methods, properties, and prospective application of these materials are summarized. Current challenges and the benefits of using biomass waste are also discussed.

The viability of large-scale biodiesel production ultimately boils down to its cost of commercialisation despite other very important factors such as the negative environmental and health effects caused by the direct combustion of fossil diesel. How much each country’s economy will be influenced by the production of biodiesel will be determined by the commitment of various stakeholders to the much-needed transition from petroleum-based resources to renewable resources. Biodiesel production is largely determined by the cost of the feedstock (>70%) and this review focuses on the use of waste oil resources as biodiesel feedstock with a special focus on waste cooking oil (WCO). Generating value from waste oil provides an alternative waste management route as well as a positive environmental and economic contribution. The transesterification process for biodiesel production, its catalysis and some important technical and economic aspects are covered in this communication with a special focus on the South African framework. An overview of the current research and its implications going forward is discussed.

The increasing rate of environmental pollution and the emergence of new infectious diseases have drawn much attention toward the area of gas sensors for air quality monitoring and early-stage disease diagnosis, respectively. Polyaniline (PANI) has become one of the extensively studied polymers in the area of chemical sensing due to its good conductivity and sensitivity at room temperature. The development of room-temperature gas sensors represents a significant leap forward in air quality monitoring by conserving energy and enhancing the feasibility of the commercial development of sensing technologies. New research shines a light on the advantages of using PANI with materials such as semiconductor metal chalcogenides, metal oxides, metal nanoparticles, and graphitic carbon materials to form composites that can sense chemicals selectively at room temperature. This review focuses on the advancements in PANI-based gas sensors, exploring the materials, mechanisms, and applications that make these sensors a promising solution for modern air quality monitoring challenges. By examining the latest research and innovations, we aim to highlight this critical technology’s potential and future directions, instilling hope and optimism in safeguarding public health and the environment.

Green chemistry seeks to find alternative synthesis routes that are less harsh to living organisms and the environment. In this communication, a microwave-assisted hydrothermal technique and a thermal annealing method were used in the reduction of graphene oxide (GO) to make reduced GO (rGO). Graphite powder was oxidised using the Improved Hummers’ method, exfoliated, and freeze-dried. Thereafter, an aqueous suspension of GO was reduced under microwave (MW) irradiation for 10 min at 600 W with and without the help of a reducing agent (hydrazine hydrate). Thermal annealing reduction was also conducted under a nitrogen atmosphere at 300 °C for 1 h. Prepared samples were analysed using Raman laser spectroscopy, X-ray diffraction (XRD), transmission electron microscopy (TEM), the Brunauer–Emmett–Teller (BET) method, and X-ray photoelectron spectroscopy (XPS). A successful reduction in the GO functional groups between the sheets was established using XRD. In the Raman analysis, the ratio of the intensity of the D and G band (I_D/I_G) in graphene sheets assisted in assessing the quality of the graphene films. An estimation of the number of structural defects was calculated using the I_D/I_G ratio. The Raman analysis showed an increase in the I_D/I_G ratio after both oxidation and reduction processes. The defect densities of both MW-treated samples were comparable while an increased defect density was evident in the thermally annealed sample. TEM micrographs confirmed the sheet-like morphology of the samples. The rGO sheets obtained from the MW-treated method appeared to be smaller when compared to the rGO ones obtained by thermal treatment. It was also evident from XRD analysis that thermal treatment promoted the coalition of graphitic layers, such that the estimated number of layers was larger than that of GO. The elemental analysis showed that the C/O ratio of GO increased from 2 to 7.8 after MW hydrazine reduction.

Herein we report on the use of different metal precursors in the synthesis of MoSe₂ nanomaterials in order to control their morphology. The use of Mo(CO)₆ as the metal precursor resulted in the formation of wrinkled few-layer nanosheets, while the use of H₂MoO₄ as the metal precursor resulted in the formation of nanoflowers. To investigate the effect of the morphologies on their performance as catalysts in the hydrogen evolution reaction, electrochemical characterization was done using linear sweep voltammetry (LSV), cyclic voltammetry (CV), and electrical impedance spectroscopy (EIS). The MoSe₂ nanoflowers were found to have superior electrochemical performance towards the hydrogen evolution reaction with a lower Tafel slope, on-set potential, and overpotential at 10 mA/cm² compared to the wrinkled few-layer nanosheets. This was found to be due to the higher effective electrochemical surface area of the nanoflowers compared to the nanosheets which suggests a higher number of exposed edge sites in the nanoflowers.