Cement is widely used as the primary binder in concrete; however, growing environmental concerns and the rapid expansion of the construction industry have highlighted the need for more sustainable alternatives. Geopolymers have emerged as promising eco-friendly binders due to their lower carbon footprint and potential to utilize industrial byproducts. Geopolymer mortar, like other cementitious substances, exhibits brittleness and tensile weakness. Basalt fibers serve as fracture-bridging reinforcements, enhancing flexural and tensile strength by redistributing loads and postponing crack growth. Basalt fibers enhance the energy absorption capacity of the mortar, rendering it less susceptible to abrupt collapse. Basalt fibers have thermal stability up to about 800–1000 °C, rendering them appropriate for geopolymer mortars designed for fire-resistant or high-temperature applications. They assist in preserving structural integrity during heat exposure. Fibers mitigate early-age microcracks resulting from shrinkage, drying, or heat gradients. This results in a more compact and resilient microstructure. Using basalt fibers improves surface abrasion and impact resistance, which is advantageous for industrial flooring or infrastructure applications. Basalt fibers originate from natural volcanic rock, are non-toxic, and possess a minimal ecological imprint, consistent with the sustainability objectives of geopolymer applications. This study investigates the mechanical and thermal performance of a geopolymer mortar composed of metakaolin and red mud as binders, with basalt powder and limestone powder replacing traditional sand. The primary objective was to evaluate the effect of basalt fiber incorporation at varying contents (0.4%, 0.8%, and 1.2% by weight) on the durability and strength of the mortar. Eight different mortar mixes were activated using sodium hydroxide (NaOH) and sodium silicate (Na₂SiO₃) solutions. Mechanical properties, including compressive strength, flexural strength, and ultrasonic pulse velocity (UPV), were tested 7 and 28 days before and after exposure to elevated temperatures (200, 400, 600, and 800 °C). The results indicated that basalt fiber significantly enhanced the performance of the geopolymer mortar, particularly at a content of 1.2%. Specimens with 1.2% fiber showed up to 20% improvement in compressive strength and 40% in flexural strength after thermal exposure, attributed to the fiber’s role in microcrack bridging and structural densification. Subsequent research should concentrate on refining fiber type, dose, and dispersion techniques to improve mechanical performance and durability. Examinations of microstructural behavior, long-term durability under environmental settings, and performance following high-temperature exposure are crucial. Furthermore, investigations into hybrid fiber systems, extensive structural applications, and life-cycle evaluations will inform the practical and sustainable implementation in the buildings.

This paper aims to study strength properties, UPV, and weight changes exposed to sulfate attack, and microstructural properties of geopolymer mortar prepared using metakaolin and red-mud as binder materials by mixing with river sand replaced partially by limestone, marble and basalt powder with different ratios (25%, 50%, and 75%) as filler materials, the mix proposed were activated by sodium silicate and sodium hydroxide solutions (12mol). The proposed samples were exposed to 10% of magnesium and sodium sulfate solutions for various periods of 60, 120, and 180 days to investigate the durability properties of the manufactured geopolymer mortar. The experimentally obtained results uncover that the prepared geopolymer mortar’s strength properties increase at 60 days for all the proposed mixes, while at 180days, the geopolymer mortar suffers a significant loss. Change in weight increase obviously between 10.83% and 13.65% for 60 days and decrease gradually for 120 days between 9.22% and 10.19% to reach a stable value between 120 and 180 days. Furthermore, to evaluate this work, the Scanning Electron Microscopy and X-ray Diffraction methods were investigated.

Rapid urbanization and industrialization have increased atmospheric pollution, particularly via sulfur oxides (SO_x) that form sulfuric acid and accelerate the degradation of cementitious materials. While Portland-cement systems have been widely studied, less is known about the acid resistance of geopolymer mortars. This study investigates the durability and microstructural evolution of metakaolin–red mud geopolymer mortars incorporating limestone, marble, and basalt powders as partial sand replacements (5, 10, and 15 wt %). Specimens were immersed in 3% H₂SO₄ for 30, 60, and 90 days, with performance evaluated via compressive and flexural strength, weight loss, and ultrasonic pulse velocity (UPV), alongside scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FTIR). After 90 days, the optimal basalt-filled mix (15 wt %) retained 84% of its initial compressive strength (46.8 MPa), compared with 61% for the control; mass loss decreased from 6.4% (control) to 3.2%, and UPV degradation was reduced by 35%. Microstructural analyses indicate denser gel phases and reduced microcracking in basalt- and marble-filled mixes. These results demonstrate that industrial by-product fillers can significantly improve sulfuric-acid resistance while supporting more sustainable binder technology.