Hydrogels wound dressings have enormous advantages due to their ability to absorb high wound exudate, capacity to load drugs, and provide quick pain relief. The use of hydrogels as wound dressings in their original form is a considerable challenge, as these are difficult to apply on wounds without support. Therefore, the incorporation of polymeric hydrogels with a certain substrate is an emerging field of interest. The present study fabricated cellulose hydrogel using the sol–gel technique and reinforced it with nonwoven cotton for sustainable wound dressing application. The nonwoven cotton was immersed inside the prepared solution of cellulose and heated at 50 °C for 2 h to form cellulose hydrogel–nonwoven cotton composites and characterized for a range of properties. In addition, the prepared hydrogel composite was also loaded with titania particles to attain antibacterial properties. The Fourier transform infrared spectroscopy and scanning electron microscopy confirmed the formation of cellulose hydrogel layers inside the nonwoven cotton structure. The fabricated composite hydrogels showed good moisture management and air permeability, which are essential for comfortable wound healing. The wound exudate testing revealed that the fluid absorptive capacity of cellulose hydrogel nonwoven cotton composite was improved significantly in comparison to pure nonwoven cotton. The results reveal the successful hydrogel formation, having excellent absorbing, antimicrobial, and sustainable properties.

In the recent era of development, the global market for the sportswear textile manufacturing industries has increased with the increase in consumption of active sportswear. The sportswear manufacturers not only focused on the market trends but also focused on material diversification with technology enhancement. The performance characteristics of active sportswear directly influence comfort level and athletic performance during sports activities. Different types of sportswear products require different performance characteristics. Appropriate moisture and heat management are the key factors for the endowment of the required physiological comfort level. In highly engineered textile-based sports goods, special characteristics are incorporated in the polymer/fibers/product manufacturing procedures/finishing techniques to obtain the maximum performance and comfort level. In this review paper current market trends, highly engineered polymers, fibers, fabrics, finishes, nanomaterials, and the recent developments in the manufacturing techniques of sportswear are illustrated.

This study introduces an innovative chemical retting approach, systematically optimized via Grey relational analysis, to achieve jute fibers that exhibit desirable characteristics of softness, high tensile strength, and suitability for spinning, with a particular focus on their application in the apparel industry. In this study, the effect of alkali treatment (alkali concentration, temperature and duration of retting) on jute fiber's chemical composition and mechanical characteristics was investigated. Jute fibers were treated at three concentrations (5 %, 10 %, 15 %) of alkali, at three different temperature (30 °C, 60 °C, & 90 °C) and for three different retting duration (12 h, 24 h, & 36 h). The surface morphology and crystallinity of fibers were analyzed using optical microscopy, X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy. The fiber linear density and mechanical characteristics were also tested. The multi-response optimization of all the factors and the responses was investigated using the Grey relational analysis. The results showed that the fiber surface morphology and crystallinity increase with an increase in alkali concentration, retting time, and temperature. Chemical retting treatment also improved the fiber linear density and tensile strength. The finest fibers which were obtained in this research had a linear density of 2.18 Tex with a tenacity of 53.02 cN/tex and elongation of 4.54 %. The spinnable jute fibers were achieved after this treatment with excellent characteristics.

Textile auxetic materials with negative Poisson’s ratio (NPR) have potential applications in protective textile, filtration, and energy absorbance. However, cotton core-spun based auxetic textile is rarely investigated. In this study, cotton core-spun (Lycra)-based helical auxetic yarn (HAY) was developed, and the effects of core filament linear density on the auxetic behavior were studied. Core-spun cotton yarns of 8/1 Nec containing core filament (180, 260, and 420 D) were developed. Then, these core-spun yarns were wrapped with 50 D Dyneema filament at 393 twist/m to make the HAY. The diameter, NPR, and tensile strength of HAY were increased with increasing linear density of Lycra filament. Image analysis of HAY containing 420 D Lycra showed 57% diameter increase with the change in axial strain from 0 to 15 mm. The maximum auxetic behavior with NPR of −3.97 and tensile strength of 26.71 cN/tex was observed in 420 D Lycra-based HAY. This study proved that the cotton core spun-based HAY can be produced with significant auxetic properties for practically potential use in wearable protective textiles.