Additive manufacturing (AM) is a sustainable and innovative manufacturing technology to fabricate products with specific properties and complex shapes for additive manufacturable materials including polymers, steels, titanium, copper, ceramics, composites, etc. This technology can well facilitate consumer needs on products with complex geometry and shape, high strength and lightweight. It is sustainable with having a layer-by-layer manufacturing process contrary to the traditional material removal technology—subtractive manufacturing. However, there are still challenges on the AM technologies, which created barriers for their further applications in engineering fields. For example, materials properties including mechanical, electrical, and thermal properties of the additively manufactured products are greatly affected by using different ways of AM methods and it was found as the material anisotropy phenomenon. In this study, a detailed literature review is conducted to investigate research work conducted on the material anisotropy phenomenon of additively manufactured materials. Based on research findings on material anisotropy phenomenon reported in the literature, this review paper aims to understand the nature of this phenomenon, address main factors and parameters influencing its severity on thermal, electrical and mechanical properties of 3D printed parts, and also, explore potential methods to minimise or mitigate this unwanted anisotropy. The outcomes of this study would be able to shed a light on improving additive manufacturing technologies and material properties of additively manufactured materials.

Nanocellulose, as a biobased versatile nanomaterial that can be derived with tailorable surface functionalities, dimensions, and morphologies, has considerable implications for modifying the rheology, mechanical reinforcement, and influencing the carbonization efficiency in the production of polyacrylonitrile (PAN)-based carbon fibers. Herein, we report the influence of three different nanocellulose types, varying in the derivatization method, source, and aspect ratio, on the mechanical properties and thermal transformations of solution-spun PAN/nanocellulose nanocomposite fibers into carbon fibers. The incorporation of 0.1 wt % nanocellulose into solution-spun PAN fibers led to a 7–19% increase in tensile modulus and 0–27% increase in tensile strength in the solution-spun fibers, compared to a control PAN fiber. These improvements varied depending on the nanocellulose type. After low-temperature carbonization at 1200 °C, improvements in the mechanical properties of the nanocellulose-reinforced carbon fibers, compared with a PAN fiber, were also observed. In contrast to the precursor fibers, the improvement % in the carbonized fibers was found to be dependent on the nanocellulose morphology and was linearly correlated with increasing aspect ratio of nanocellulose. For example, in carbon fibers with a cotton-derived low-aspect-ratio cellulose nanocrystal and spinifex-derived high-aspect-ratio CNC and nanofiber, up to 4, 87, and 172% improvements in tensile moduli were observed, respectively. Due to the processing methods used, the nanocellulose aspect ratio and crystallinity are inversely related, and as such, the increase in the carbon fiber mechanical properties was also related to a decrease in crystallinity of the nanocellulose reinforcers. Raman spectra and electron microscopy analysis suggest that mechanical improvement after carbonization is due to internal reinforcement by highly ordered regions surrounding the carbonized nanocellulose, within the turbostratic carbon fibers.

Boron removal capacity of multi-walled carbon nanotubes (MWCNTs) modified with tartaric acid was investigated in this study. Modification of MWCNTs with tartaric acid was confirmed by Boehm surface chemistry method and fourier transform infra-red (FT-IR) spectroscopy. Experiments were performed to determine the adsorption isotherm and adsorption thermodynamic parameters of boron adsorption on tartaric acid modified MWCNTs (TA-MWCNTs). The effect of variables including initial pH, dosage of adsorbent, contact time and temperature was investigated. Analysis of data showed that adsorption equilibrium could be better described by Freundlich isotherm and the maximum adsorption capacities obtained at the pH of 6.0 was 1.97 mg/g. The estimated thermodynamic values of free energy (ΔG°), entropy (ΔS°) and enthalpy (ΔH°) indicated a spontaneous and an endothermic process. Furthermore, the TA-MWCNTs was magnetized for separation of boron-contaminated adsorbent from aqueous solution by applying magnetic field. The results showed that magnetic TA-MWCNTs particles were separated effectively after adsorption from contaminated water.