Tensile and viscoelastic properties of collagen fascicles of approximately 300 μm in diameter, which were obtained from rabbit patellar tendons, were studied using a newly designed micro-tensile tester. Their cross-sectional areas were determined with a video dimension analyzer combined with a CCD camera and a low magnification microscope. There were no statistically significant differences in tensile properties among the fascicles obtained from six medial-to-lateral locations of the patellar tendon. Tangent modulus, tensile strength, and strain at failure of the fascicles determined at about 1.5 percent/s strain rate were 216 ± 68 MPa, 17.2 ± 4.1 MPa, and 10.9 ± 1.6 percent (mean ± S.D.), respectively. These properties were much different from those of bulk patellar tendons; for example, the tensile strength and strain at failure of these fascicles were 42 percent and 179 percent of those of bulk tendons, respectively. Tangent modulus and tensile strength of collagen fascicles determined at 1 percent/s strain rate were 35 percent larger than those at 0.01 percent/s. The strain at failure was independent of strain rate. Relaxation tests showed that the reduction of stress was approximately 25 percent at 300 seconds. These stress relaxation behavior and strain rate effects of collagen fascicles differed greatly from those of bulk tendons. The differences in tensile and viscoelastic properties between fascicles and bulk tendons may be attributable to ground substances, mechanical interaction between fascicles, and the difference of crimp structure of collagen fibrils.

With the aim of studying mechanisms of the remodeling of tendons and ligaments, the effects of stress shielding on the rabbit patellar tendon were studied by performing tensile and stress relaxation tests in the transverse direction. The tangent modulus, tensile strength, and strain at failure of non-treated, control patellar tendons in the transverse direction were 1272 kPa, 370 kPa, and 40.5 percent, respectively, whereas those of the tendons stress-shielded for 1 week were 299 kPa, 108 kPa, and 40.4 percent, respectively. Stress shielding markedly decreased tangent modulus and tensile strength in the transverse direction, and the decreases were larger than those in the longitudinal direction, which were determined in our previous study. For example, tensile strength in the transverse and longitudinal direction decreased to 29 and 50 percent of each control value, respectively, after 1 week stress shielding. In addition, the stress relaxation in the transverse direction of stress-shielded patellar tendons was much larger than that of non-treated, control ones. In contrast to longitudinal tensile tests for the behavior of collagen, transverse tests reflect the contributions of ground substances such as proteoglycans and mechanical interactions between collagen fibers. Ground substances provide lubrication and spacing between fibers, and also confer viscoelastic properties. Therefore, the results obtained from the present study suggest that ground substance matrix, and interfiber and fiber–matrix interactions have important roles in the remodeling response of tendons to stress. [S0148-0731(00)00806-2]

In-vitro tissue culture experiments were performed to study the effects of static stress on the mechanical properties of collagen fascicles obtained from the rabbit patellar tendon. After collagen fascicles having the diameter of approximately 300 μm were cultured for 1 and 2 wk under static stress between 0 and 3 MPa, their mechanical properties and crimp morphology were determined using a micro-tensile tester and a light microscope, respectively. The tensile strength and tangent modulus of the fascicles were significantly decreased by culture under no load compared to control fascicles. A statistically significant correlation, which was described by a quadratic curve, was observed between applied stress and tensile strength. The maximum tensile strength (16.7 MPa) was obtained at the applied stress of 1.2 MPa; the strength was within a range of control values. There was a similar correlation between applied stress and tangent modulus, and the modulus was maintained at control level under 1.3 MPa stress. The stress of 1.2 to 1.3 MPa is equivalent to approximately 50 percent of the peak stress developed in the intact rabbit patellar tendon by running. Strain at failure of cultured collagen fascicles was negatively correlated with applied stress, and that at 1.2 to 1.3 MPa stress was almost the same as the control value. Crimp morphology in the fascicles cultured under about 1.2 MPa stress was similar to that in control fascicles. These results indicate that cultured collagen fascicles change the mechanical properties and structure in response to static tensile stress. In addition, their mechanical properties and structure are maintained at control level if the static stress of 50 percent of in-vivo peak stress is applied.