Amphiphilic block polypeptides of poly(sarcosine)-b-(l- or d-Leu-Aib)₆ (SL12OMe or SD12OMe) and poly(sarcosine)-b-(l-Leu-Aib)₇ (SL14OMe) were reported to self-assemble into a nanotube morphology. Herein, we tried to construct a phase-separated nanotube by sticking two different kinds of nanotubes. SD12OMe nanotubes were found to stick to SL14OMe nanotubes with a heat treatment at 50 °C, but the sticking yield was limited. The amphiphilic polypeptides were functionalized by replacement of methyl ester with aromatic groups of N-ethylcarbazole (SL12Ecz) and naphthalimide (SD12NpiTEG), but they lost the ability to form homogeneous nanotubes. A fraction of the functionalized amphiphilic polypeptides mixing in the nanotube-forming amphiphilic polypeptides, a mixture of SL12OMe and SL12Ecz (9:1) as well as a mixture of SD12OMe and SD12NpiTEG (9:1), allowed nanotube formation. These two kinds of nanotubes partly stuck together with a heat treatment at 15 °C to maintain a segregated state of two kinds of aromatic groups along the nanotube, resulting in the formation of a phase-separated nanotube.

The introduction of α-helical structure with a specific helix–helix interaction into an amphipathic molecule enables the determination of the molecular packing in the assembly and the morphological control of peptide assemblies. We previously reported that the amphiphilic polypeptide SL12 with a polysarcosine (PSar) hydrophilic chain and hydrophobic α-helix (l-Leu-Aib)₆ involving the LxxxLxxxL sequence, which induces homo-dimerization due to the concave–convex interaction, formed a nanotube with a uniform 80 nm diameter. In this study, we investigated the importance of the LxxxLxxxL sequence for tube formation by comparing amphiphilic polypeptide SL4A4L4 with hydrophobic α-helix (l-Leu-Aib)₂-(l-Ala-Aib)₂-(l-Leu-Aib)₂ and SL12. SL4A4L4 formed spherical vesicles and micelles. The effect of the LxxxLxxxL sequence elongation on tube formation was demonstrated by studying assemblies of PSar-b-(l-Ala-Aib)-(l-Leu-Aib)₆-(l-Ala-Aib) (SA2L12A2) and PSar-b-(l-Leu-Aib)₈ (SL16). SA2L12A2 formed nanotubes with a uniform 123 nm diameter, while SL16 assembled into vesicles. These results showed that LxxxLxxxL is a necessary and sufficient sequence for the self-assembly of nanotubes. Furthermore, we fabricated a double-layer nanotube by combining two kinds of nanotubes with 80 and 120 nm diameters—SL12 and SA2L12A2. When SA2L12A2 self-assembled in SL12 nanotube dispersion, SA2L12A2 initially formed a rolled sheet, the sheet then wrapped the SL12 nanotube, and a double-layer nanotube was obtained.