Uncontrolled bleeding and infection can cause significant increases in mortalities. Hydrogel sealants have attracted extensive attention for their ability to control bleeding. However, because interfacial water is a formidable barrier to strong surface bonding, a challenge remains in finding a product that offers robust tissue adhesion combined with anti-infection properties. Inspired by the strong adhesive mechanism of biofilm and mussels, we report a novel dual bionic adhesive hydrogel (DBAH) based on chitosan grafted with methacrylate (CS-MA), dopamine (DA), and N-hydroxymethyl acrylamide (NMA) via a facile radical polymerization process. CS-MA and DA were simultaneously included in the adhesive polymer for imitating the two key adhesive components: polysaccharide intercellular adhesin (PIA) of staphylococci biofilm and 3,4-dihydroxy-l-phenylalanine (Dopa) of mussel foot protein, respectively. DBAH presented strong adhesion at 34 kPa even upon three cycles of full immersion in water and was able to withstand up to 168 mm Hg blood pressure, which is significantly higher than the 60–160 mm Hg measured in most clinical settings. Most importantly, these hydrogels presented outstanding hemostatic capability under wet and dynamic in vivo movements while displaying excellent antibacterial properties and biocompatibility. Therefore, DBAH represents a promising class of biomaterials for high-efficiency hemostasis and wound healing.

Endophytes have the potential to enhance the ability of plants to resist salt stress, improving crop development and yield. Therefore, in this study, we isolated an endophyte that produced large amounts of exopolysaccharides (EPSs) from the roots of sea rice and examined its effects on the physiological responses of rice (Oryza sativa L. ssp. japonica “Nipponbare”) seedlings to salt stress using hydroponic experiments. The endophyte was named Pantoea alhagi NX-11 based on its morphological characteristics and 16S ribosomal DNA (rDNA) sequence alignment. Rice seedlings that had been inoculated with P. alhagi NX-11 exhibited a 30.3% increase in fresh weight, a 28.6% increase in root length, a 51.6% increase in shoot length, and a 26.3% increase in chlorophyll content compared with control seedlings under normal conditions. In addition, inoculated rice seedlings had a 37.5% lower malondialdehyde content, a 133% higher K⁺/Na⁺ ratio, and a 52.8% higher proline content after 7 days under salt stress, as well as up-regulated expression of proline synthase, down-regulated expression of proline dehydrogenase, and enhanced antioxidant enzyme activities. Interestingly, rice seedlings that were inoculated with an EPS-deficient strain named NX-11^eps– that was obtained by atmospheric and room temperature plasma (ARTP) mutagenesis were damaged by salt stress and had similar physiological and biochemical indicators to the control group. Therefore, we speculate that the ability of P. alhagi NX-11 to enhance the salt tolerance of rice seedlings is related to the EPSs it produces.

Injectable hydrogels are promising candidates for adhesives because of their ease of administration, minimal invasion, and biocompatibility. While developing surgical adhesives with strong wet tissue adhesion, controlled degradability and mechanical properties, and excellent biocompatibility have still been a significant challenge. Herein, inspired from nature, we report a novel mussel-inspired tissue-adhesive hydrogel composed of poly(γ-glutamic acid) and dopamine (γ-PGA–DA) that can bond tissues well and stop bleeding in a wet environment by improving its tissue adhesiveness via a horseradish peroxidase-mediated reaction. The hydrogel exhibited 10–12 fold stronger wet tissue adhesion strength (58.2 kPa) over the clinically used fibrin glue and more effective hemostatic ability following liver impalement in animal models (41.2% reduction in the average amount of bleeding compared with fibrin glue). In addition, the hydrogels demonstrated controlled gelation time, swelling ratio, microscopic morphology, biodegradability and tissue-like elastomeric mechanical properties, and exhibited excellent cyto/tissue-compatibility. The overall results suggest that the γ-PGA–DA hydrogels can be considerably applied as promising wet-resistant adhesives and hemostatic materials.