Single‐layered MoS₂ is a promising anode material for lithium‐ion batteries (LIBs), sodium‐ion batteries (SIBs), and potassium‐ion batteries (PIBs) due to its high capacity and isotropic ion transport paths. However, the low intrinsic conductivity and easy‐agglomerated feature hamper its applications. Here, a charge‐driven interlayer expansion strategy that Co²⁺ replaces Mo⁴⁺ in the doping form to endow MoS₂ layers with negative charges, thus inducing electrostatic repulsion, together with the insertion of gaseous groups, to drive interlayer expansion which once breaks the confinement of interlayer van der Waals force, single‐layered MoS₂ is obtained and uniformly dispersed into carbon matrix arising from the transformation of carbonaceous gaseous groups under high vapor pressure, is proposed. Co atom doping helps enhance the intrinsic conductivity of single‐layered MoS₂. Carbon matrix effectively prevents agglomeration of single‐layered MoS₂. The doped Co atoms can be fully transformed into ultrasmall Co nanoparticles during conversion reaction, which enables strong spin‐polarized surface capacitance and thus significantly boosts ion transport and storage. Consequently, the prepared material delivers superb Li/Na/K‐ion storage performances, which are best in the reported MoS₂‐based anodes. The proposed charge‐driven interlayer expansion strategy provides a novel perspective for preparing single‐layered MoS_2, which shows huge potential for energy storage.

The utilization of recycled coarse aggregate (RCA) from construction and demolition waste (CDW) is a sustainable solution to protect the fragile natural environment and save the diminishing natural resources. The current study was aimed at exploring the impact resistance and mechanical properties of recycled aggregate concrete (RAC) affected by hooked-end steel fiber (HF) and crimped steel fiber (CF). Fifteen concrete mixtures considering different RCA substitution ratio, steel fiber dosage, and steel fiber shapes were designed. Meanwhile, a statistical analysis method-based Weibull distribution was introduced to evaluate the variations of impact test results, presented using a reliability function. Lastly, the microstructural morphologies of interfacial transition zones at the cement paste/aggregate and cement paste/fiber interfaces were observed using a scanning electron microscope (SEM). The experimental results showed that the impact resistance and mechanical properties mildly decreased with the increase in substitution ratio of RCA, whereas they conclusively increased with the increase in steel fiber content. Steel fiber recycled aggregate concrete (SFRAC) with 1.5% steel fiber content had the best impact resistance, and its initial cracking times and final failure times were 3.25–4.75 and 8.78–29.08 times those of plain RAC, respectively. HF has better impact resistance than CF. The SEM observations of microstructures indicated that the hardened cement paste of natural aggregate concrete (NAC) was more compact than that of RAC. Steel fiber had a better connection with the cement paste interface than that of aggregate and cement paste owing to better thermal conductivity. This research could be a guide for SFRAC as a structural material in practical engineering, steering the construction industry toward the circular economy.

In order to reduce the manufacturing cost of foamed ceramics and expand the application scope of industrial solid waste, in this study, a new type of environment-friendly foamed ceramics was prepared using direct high-temperature foaming with waste silicomanganese slag (SMS) and fly ash (FA) as raw materials and silicon carbide (SiC) as a foaming agent. The influence of SMS content, SiC content, and sintering temperature on the characteristics and microstructure of the specimen were explored. More concretely, the compressive strength, pore morphology, bulk density, and crystalline composition of the foamed ceramics were discussed. The foaming mechanism was also further analyzed. The results showed that including 20% SMS significantly reduced the melt’s viscosity and stimulated bubble expansion. This, in turn, facilitated the creation of a porous structure. Moreover, it was noted that samples containing 20% SMS exhibited an anorthite phase when sintered at 1110 °C, resulting in enhanced compressive strength. The bulk density and compressive strength of the foamed ceramics decreased with an increase in the sintering temperature and SiC content. This trend was primarily attributed to the higher total porosity and the insufficient support of the pore wall to the matrix. The best all-around performance was achieved with 20 wt% SMS, 80 wt% FA as raw material, SiC addition of 1.0 wt%, and a sintering temperature of 1100 °C. Under these conditions, the compressive strength, bulk density, and total porosity of the foamed ceramics were 8.09 MPa, 0.57 g/cm³, and 71.04%, respectively. Taken together, the outstanding porous structure and mechanical properties of this foamed ceramic make it suitable for use as insulation or for building partition materials.