Sheets of polycaprolactone (PCL) and ultra-high molecular weight polyethylene (UHMWPE) were fabricated and shaped by the Single-Point Incremental Forming process (SPIF). The performance of these biocompatible polymers in SPIF was assessed through the variation of four main parameters: the diameter of the forming tool, the spindle speed, the feed rate, and the step size based on a Box–Behnken design of experiments of four variables and three levels. The design of experiments allowed us to identify the parameters that most affect the forming of PCL and UHMWPE. The study was completed by means of a deep characterization of the thermal and structural properties of both polymers. These properties were correlated to the performance of the polymers observed in SPIF, and it was found that the polymer chains are oriented as a consequence of the SPIF processing. Moreover, by X-ray diffraction it was proved that polymer chains behave differently on each surface of the fabricated parts, since the chains on the surface in contact with the forming tool are oriented horizontally, while on the opposite surface they are oriented in the vertical direction. The unit cell of UHMWPE is distorted, passing from an orthorhombic cell to a monoclinic due to the slippage between crystallites. This slippage between crystallites was observed in both PCL and UHMWPE, and was identified as an alpha star thermal transition located in the rubbery region between the glass transition and the melting point of each polymer.

Environmental contaminants constitute an ecological and health hazard, which requires green sensing. The RAFT-MIP approach for tailor-made selective receptors enhances themviabinding affinities for use in environmental contaminant sensors.

Product miniaturization is a constant trend in industries that demand ever-smaller products that can be mass produced while maintaining high precision dimensions in the final pieces. Ultrasonic micro injection molding (UMIM) technology has emerged as a polymer processing technique capable of achieving the mass production of polymeric parts with micro-features, while still assuring replicability, repeatability, and high precision, contrary to the capabilities of conventional processing technologies of polymers. In this study, it is shown that the variation of parameters during the UMIM process, such as the amplitude of the ultrasound waves and the processing time, lead to significant modification on the molecular structure of the polymer. The variation of both the amplitude and processing time contribute to chain scission; however, the processing time is a more relevant factor for this effect as it is capable of achieving a greater chain scission in different areas of the same specimen. Further, the presence of polymorphism within the samples produced by UMIM is demonstrated. Similarly to conventional processes, the UMIM technique leads to some degree of chain orientation, despite the fact that it is carried out in a relatively small time and space. The results presented here aim to contribute to the optimization of the use of the UMIM process for the manufacture of polymeric micro parts.