The aim of the present study was to evaluate the fracture loads of polymethyl methacrylate (PMMA) complete denture bases reinforced with glass-fiber mesh and orthopedic casting tape (OCT) in comparison to conventional PMMA dentures under artificial aging. Dental fiberglass framework (Group 1) and OCT (Group 2 and 3) reinforced PMMA acrylic dentures were fabricated on the edentulous ridge. Ten PMMA dentures without reinforcement (Group 4) were included as controls. All specimens were placed in a chewing simulator chamber, and fatigue load was applied. To assess the fracture loads, static loads with a universal testing machine were applied. Fractured specimens in each group were evaluated under a scanning electron microscope. The data were statistically analyzed employing analysis of variance and Tukey post-hoc test. The association of denture weight and thickness on fracture load was assessed using Pearson and Spearman correlations. Dental fiberglass (Group 1) displayed the highest fracture load (692.33 ± 751.41 N), and Group 4 (control) exhibited the lowest fracture loads (281.41 ± 302.51 N). Dentures reinforced with fiberglass mesh framework exhibited intact fractures. In contrast, Group 2 and 3 specimens using OCT demonstrated ditching fractures. It was observed that the thickness and weight of all the reinforced specimens influenced the load required to fracture the dentures (p < 0.001). Denture specimens strengthened with OCT (Groups 2 and 3) exhibited failure loads lower than dental fiberglass (Group 1) specimens but higher than unreinforced controls.

The aim was to identify the influence of conventional polymeric resin based cement (RC), hybrid polymer modified glass ionomer (RMGIC) and Zinc phosphate cement (ZPC) on the pull out strength of the customized zirconia post in premolars. Access cavity and root canals were performed in sixty premolar teeth with the standardized crown down technique (ProTaper Universal, Dentsply). Post space impressions were scanned, and the pre-sintered Zenostar Zr Translucent blanks (Weiland Dental, Pforzheim) were milled with the Opera-system to form the post. All prepared specimens were divided equally in three groups based on the cement type employed for luting as follows: group A: ZPC; group B (GC Fuji PLUS Capsule): RMGIC; group C (and RC (3M RelyX ARC). Ten specimens in each group were thermocycled (TC) at 5 and 55 °C in distilled water baths (40,000 cycles). Pull out bond strength was assessed using a universal testing machine at 0.5 mm/min. The means and standard deviations were compared using ANOVA and Tukey Kramer multiple comparisons tests. A significant difference among the cement groups as well as between TC and non-thermocycled (NTC) groups (p < 0.05) was observed. The highest tensile stress was demonstrated among group C (Resin, 69.89 ± 4.81 (NTC), 64.06 ± 4.36 (TC)) with the least in group A, (zinc phosphate, 43.66 ± 5.02 (NTC), 37.70 ± 5.10 (TC)) for both groups. Group A presented with 100% adhesive bond failures, followed by 80% in group C and 70% in group B, respectively. A similar outcome was observed in the TC group for the cement; however, unlike the NTC group, the TC group showed more cohesive failures compared to the NTC mixed failure. Dual cure polymer based cement demonstrated higher bond strength and efficient adhesive bonding of the customized Zr post with root dentine compared to zinc phosphate (non-polymeric) and RMGIC (hybrid polymer). Thermocycling compromised Zr post adhesive bonding to root dentin.

This case aimed to assess the clinical and radiographic outcomes of the All‐on‐4 and the All‐on‐6 concept using three‐dimensional computer‐assisted treatment planning, and computer‐guided surgery. Two years after the treatment, the “All‐on‐4” and “All‐on‐6” concepts provided effective treatment for immediate restoration and showed predictable outcomes in a completely edentulous patient.

Various disinfecting agents showing variable success in disinfecting polymethyl methacrylate (PMMA) are available. The aim of our study was to evaluate the antifungal efficacy of sodium perborate (denture cleaning tablet-DC), microwave irradiation, and their combination for eradicating candida albicans (C. albicans) from polymethyl methacrylate (PMMA) denture base polymer. One hundred and sixty-eight PMMA resin specimens (30 × 30 × 15 mm) were divided into four groups, including control (no disinfection), microwave disinfection in distilled water (MW-DW), sodium perborate with distilled water (DC-DW), and a combination of MW-DC-DW (n = 10). Biofilms of C. albicans were cultured on the PMMA resin denture base specimens for 96 h. The samples were exposed to three different antifungal regimes, i.e., MW, denture cleaning agent-sodium perborate (DC) and DW, and a combination of MW-DC-DW for 1 to 5 min. Scanning electron microscopy (SEM) was performed to evaluate colony formation. The colony-forming units (CFU) among the experimental groups were assessed using ANOVA, a Kruskal–Wallis test, and a Mann–Whitney test. The mean CFU values were compared with the control for each disinfecting regime at 96 h growth time. For MW-DC-DW, the CFU were significantly low at 2 and 3 min of exposure when compared with the control (DW) (p < 0.05). For the MW-DW treated group, the CFU were significantly low at 3 min of exposure when compared with the control (DW) (p < 0.05). It was also found that for DC-DW, the CFU were significantly low at 5 minutes when compared with the control specimens (DW) (p < 0.05). Microwave disinfection in combination with sodium perborate is a more effective disinfecting regime against C. albicans than that of microwave disinfection and sodium perborate alone.