In the present work, the effectiveness of four non-halogenated flame retardants (FR) (aluminium trihydroxide (ATH), magnesium hydroxide (MDH), Sepiolite (SEP) and a mix of metallic oxides and hydroxides (PAVAL)) in blends with recycled acrylonitrile-butadiene-styrene (rABS) was studied in order to develop a more environmentally friendly flame-retardant composite alternative. The mechanical and thermo-mechanical properties of the obtained composites as well as their flame-retardant mechanism were evaluated by UL-94 and cone calorimetric tests. As expected, these particles modified the mechanical performance of the rABS, increasing its stiffness at the expense of reducing its toughness and impact behavior. Regarding the fire behavior, the experimentation showed that there is an important synergy between the chemical mechanism provided by MDH (decomposition into oxides and water) and the physical mechanism provided by SEP (oxygen barrier), which means that mixed composites (rABS/MDH/SEP) can be obtained with a flame behavior superior to that of the composites studied with only one type of FR. In order to find a balance between mechanical properties, composites with different amounts of SEP and MDH were evaluated. The results showed that composites with the composition rABS/MDH/SEP: 70/15/15 wt.% increase the time to ignition (TTI) by 75% and the resulting mass after ignition by more than 600%. Furthermore, they decrease the heat release rate (HRR) by 62.9%, the total smoke production (TSP) by 19.04% and the total heat release rate (THHR) by 13.77% compared to unadditivated rABS; without compromising the mechanical behavior of the original material. These results are promising and potentially represent a greener alternative for the manufacture of flame-retardant composites.

An understanding of the mechanical behavior of polymeric materials is crucial for making advancements in the applications and efficiency of nanocomposites, and encompasses their service life, load resistance, and overall reliability. The present study focused on the prediction of the mechanical behavior of biopolymeric nanocomposites with nano-clays as the nanoadditives, using a new modeling and simulation method based on Comsol Multiphysics software 6.1. This modeling considered the complex case of flake-shaped nano-clay additives that could form aggregates along the polymeric matrix, varying the nanoadditive thickness, and consequently affecting the resulting mechanical properties of the polymeric nanocomposite. The polymeric matrix investigated was biopolyamide 11 (BIOPA11). Several BIOPA11 samples reinforced with three different contents of nano-clays (0, 3, and 10 wt%), and with three different nano-clay dispersion grades (employing three different extrusion screw configurations) were obtained by the compounding extrusion process. The mechanical behavior of these samples was studied by the experimental tensile test. The experimental results indicate an enhancement of Young’s modulus as the nano-clay content was increased from 0 to 10 wt% for the same dispersion grades. In addition, the Young’s modulus value increased when the dispersion rate of the nano-clays was improved, showing the highest increase of around 93% for the nanocomposite with 10 wt% nano-clay. A comparison of the modeled mechanical properties and the experimental measurements values was performed to validate the modeling results. The simulated results fit well with the experimental values of Young’s modulus.

This article presents, for the first time, the results of applying the rheological technique to measure the molecular weights (Mw) and their distributions (MwD) of highly hierarchical biomolecules, such as non-hydrolyzed collagen gels. Due to the high viscosity of the studied gels, the effect of the concentrations on the rheological tests was investigated. In addition, because these materials are highly sensitive to denaturation and degradation under mechanical stress and temperatures close to 40 °C, when frequency sweeps were applied, a mathematical adjustment of the data by machine learning techniques (artificial intelligence tools) was designed and implemented. Using the proposed method, collagen fibers of Mw close to 600 kDa were identified. To validate the proposed method, lower Mw species were obtained and characterized by both the proposed rheological method and traditional measurement techniques, such as chromatography and electrophoresis. The results of the tests confirmed the validity of the proposed method. It is a simple technique for obtaining more microstructural information on these biomolecules and, in turn, facilitating the design of new structural biomaterials with greater added value.

The aim of this study is the preparation of star-shaped branched polyamides (sPA6) with low melt viscosity, but also with improved mechanical properties by reactive extrusion. This configuration has been obtained by grafting a tri-functional, three-armed molecule: 5-aminoisophthalic-acid, used as a linking agent (LA). The balance between the fluidity, polarity and mechanical properties of sPA6s is the reason why these materials have been investigated for the impregnation of fabrics in the manufacture of thermoplastic composites. For these impregnation processes, the low viscosity of the melt has allowed the processing parameters (temperature, pressure and time) to be reduced, and its new microstructure has allowed the mechanical properties of virgin thermoplastic resins to be maintained. A significant improvement in the ultrasonic welding processes of the composites was also found when an energy director based on these materials was applied at the interface. In this work, an exhaustive microstructural characterization of the obtained sPAs is presented and related to the final properties of the composites obtained by film stacking.