Semiconductor TiO₂ photocatalysis has attracted much attention due to its potential application in solving the problems of environmental pollution. In this paper, thiourea (CH₄N₂S) modified anatase TiO₂ nanorods were fabricated by calcination of the mixture of TiO₂ nanorods and thiourea at 600 °C for 2 h. It was found that only N element was doped into the lattice of TiO₂ nanorods. With increasing the weight ratio of thiourea to TiO₂ (R) from 0 to 8, the light-harvesting ability of the photocatalyst steady increases. Both the crystallization and photocatalytic activity of TiO₂ nanorods increase first and then decrease with increase in R value, and R2 sample showed the highest crystallization and photocatalytic activity in degradation of Brilliant Red X3B (X3B) and Rhodamine B (RhB) dyes under visible light irradiation (λ > 420 nm). The increased visible-light photocatalytic activity of the prepared N-doped TiO₂ nanorods is due to the synergistic effects of the enhanced crystallization, improved light-harvesting ability and reduced recombination rate of photo-generated electron-hole pairs. Note that the enhanced visible photocatalytic activity of N-doped nanorods is not based on the scarification of their UV photocatalytic activity.

Bimetallic zeolite Beta in bead format and containing Al sites with Brønsted acid behavior and Sn, Zr or Hf sites with Lewis acid character, were prepared using a two-step synthetic route. First, zeolite Beta in the format of macroscopic beads (400 to 840 μm) with hierarchical porosity (micropores accessed through meso- and macropores in the range of 30 to 150 nm) were synthesized by hydrothermal crystallization in the presence of anion-exchange resin beads as hard template and further converted into their H-form. Next, the zeolite beads were partially dealuminated using different concentrations of HNO₃ (i.e., 1.8 or 7.2 M), followed by grafting with one of the above-mentioned metals (Sn, Zr or Hf) to introduce Lewis acid sites. These bimetallic zeolites were tested as heterogeneous catalysts in the conversion of dihydroxyacetone (DHA) to methyl lactate (ML). The Sn-containing zeolite Beta beads treated by 1.8 M HNO₃ and grafted with 27 mmol of SnCl₄ (Sn-deAl-1.8-Beta-B) demonstrated the best catalytic activity among the prepared bimetallic zeolite beads, with 99% selectivity and 90% yield of ML after 6 h at 90 °C. This catalyst was also tested in combination with Au-Pd nanoparticles supported on functionalized carbon nanotubes (CNTs) as multifunctional catalytic system for the conversion of glycerol to ML, achieving 29% conversion of glycerol and 67% selectivity towards ML after 4.5 h at 140 °C under 30 bar air. The catalytic results were rationalized by means of a thorough characterization of the zeolitic beads with a combination of techniques (XRD, N₂-physisorption, SEM, XRF, TEM, UV-vis spectroscopy and pyridine-FT-IR).