The determination of microstructural details for powder materials is vital for facilitating their selective laser melting (SLM) process. Four widely used steels (316L, H13, P20 and 18Ni300) have been investigated to detail their powders’ microstructures as well as laser absorptivity to understand their SLM processing from raw material perspective. Phase components of these four steel powders were characterized by X-ray diffraction (XRD), synchrotron radiation X-ray diffraction (SR-XRD) and scanning electron microscopy (SEM). X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) were utilized to reveal the surface structure of these four steel powders. It is found that phase components of H13, P20 and 18Ni300 are mainly composed of martensite and a small amount of austenite due to the high cooling rate during gas atomization processing, while 316L is characterized by austenite. XPS results show that the four steel powders all possess a layered surface structure, consisting of a thin iron oxide layer at the outmost surface and metal matrix at the inner surface. It is found that the presence of such oxide layer can improve the absorptivity of steel powders and is beneficial for their SLM process.

One of the bottleneck issues for commercial scale-up of Ti additive manufacturing lies in high cost of raw material, i.e. the spherical Ti powder that is often made by gas atomization. In this study, we address this significant issue by way of powder modification & ball milling processing, which shows that it is possible to produce printable Ti powders based on ultra-low cost, originally unprintable hydrogenation-dehydrogenation (HDH) Ti powder. It is also presented that the as-printed Ti using the modified powder exhibits outstanding mechanical properties, showing a combination of excellent fracture strength (~895 MPa) and high ductility (~19.0% elongation).