We report the superconductivity at above 30 K in a FeSe-layer compound K0.8Fe2Se2 (nominal composition) achieved by metal K intercalating in between FeSe layers. It is isostructural to BaFe2As2 and possesses the highest Tc for FeSe-layer materials so far under ambient pressure. Hall effect indicates the carriers are dominated by electron in this superconductor. We confirm that the observed superconductivity at above 30 K is due to this FeSe-based 122 phase. Our results demonstrate that FeSe-layer materials are really remarkable superconductors via structure and carrier modulation.

T graphene, a two-dimensional carbon allotrope with tetrarings, is investigated by first-principles calculations. We demonstrate that buckled T graphene has Dirac-like fermions and a high Fermi velocity similar to graphene even though it has nonequivalent bonds and possesses no hexagonal honeycomb structure. New features of the linear dispersions that are different from graphene are revealed. $\pi${} and $\pi${}* bands and the two comprising sublattices are the key factors for the emergence of Dirac-like fermions. T graphene and its two types of nanoribbon are expected to possess additional properties over graphene due to its different band structure.

New iron selenide superconductors by intercalating smaller-sized alkali metals (Li, Na) and alkaline earths using high-temperature routes have been pursued ever since the discovery of superconductivity at about 30 K in KFe₂Se₂, but all have failed so far. Here we demonstrate that a series of superconductors with enhanced T_c = 30∼46 K can be obtained by intercalating metals, Li, Na, Ba, Sr, Ca, Yb, and Eu in between FeSe layers by the ammonothermal method at room temperature. Analysis on their powder X-ray diffraction patterns reveals that all the main phases can be indexed based on body-centered tetragonal lattices with a∼3.755–3.831 Å while c∼15.99–20.54 Å. Resistivities show the corresponding sharp transitions at 45 K and 39 K for NaFe₂Se₂ and Ba_0.8Fe₂Se₂, respectively, confirming their bulk superconductivity. These findings provide a new starting point for studying the properties of these superconductors and an effective synthetic route for the exploration of new superconductors as well.

Defect-induced magnetism is firstly observed in neutron irradiated SiC single crystals. We demonstrated that the intentionally created defects dominated by divacancies (VSiVC) are responsible for the observed magnetism. First-principles calculations revealed that defect states favor the formation of local moments and the extended tails of defect wave functions make long-range spin couplings possible. Our results confirm the existence of defect-induced magnetism, implying the possibility of tuning the magnetism of wide band-gap semiconductors by defect engineering.