Although titanium‐zirconium (Ti‐Zr) alloy has been adopted for clinical applications, the ideal proportion of Zr in the alloy has not been identified. In this study, we investigated the biocompatibility of Ti‐Zr alloy by evaluating its corrosion resistance to better understand whether there is an optimal range or value of Zr proportion in the alloy. We prepared pure Ti, Ti‐30Zr, Ti‐50Zr, Ti‐70Zr, and pure Zr (mol% of Zr) samples and subjected them to anodic polarization and immersion tests in a lactic acid + sodium chloride (NaCl) solution and artificial saliva. We observed pitting corrosion in the Ti‐70Zr and Zr after exposure to both solutions. After the immersion test, we found that pure Ti exhibited the greatest degree of dissolution in the lactic acid + NaCl solution, with the addition of Zr dramatically reducing Ti ion dissolution, with the reduction ultimately exceeding 90% in the case of the Ti‐30Zr. Hence, although the localized corrosion resistance under severe conditions was compromised when the Zr content was more than 70%, metal ion release reduced owing to Zr addition and the corresponding formation of a stable passive layer. The results suggest that Ti‐30Zr or a Zr proportion of less than 50% would offer an ideal level of corrosion resistance for clinical applications. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 106B: 73–79, 2018.

Binary titanium-zirconium alloys have been studied as promising alternatives for Ti implants. The commercial Ti-15Zr alloy (Roxolid, Straumann) has been the major subject of numerous binary Ti-Zr alloys-related studies and has gained wide recognition in laboratory studies and clinical practices. However, binary Ti-Zr alloys of other composition ratios are still being investigated by researchers. This review aims to provide information on the potential of binary Ti-Zr alloys other than Ti-15Zr as implant materials in terms of mechanical strengths, chemical or electrochemical corrosion resistance capabilities, and biological performances. In addition, in this review, the Ti-15Zr alloy is discussed only when compared with other binary Ti-Zr alloys. From the included 26 studies, it is confirmed that the mechanical, chemical, electrochemical, and biological properties of Ti-Zr alloys are related to the Ti and Zr composition ratio in the alloy, phase, manufacturing process, and surface treatment. Among the studied alloys, α-or α' phase-Ti-5 wt, 45 wt/30at, and 50 wt. %Zr exhibited relatively more promising results for further investigation. More research is necessary to evaluate the potential for future use of these materials for implants.

Peri-implantitis is an unsolved but critical problem with dental implants. It is postulated that creating a seal of gingival soft tissue around the implant neck is key to preventing peri-implantitis. The objective of this study was to determine the effect of UV surface treatment of titanium disks on the adhesion strength and retention time of oral connective tissues as well as on the adherence of mucosal fibroblasts. Titanium disks with a smooth machined surface were prepared and treated with UV light for 15 min. Keratinized mucosal tissue sections (3 × 3 mm) from rat palates were incubated for 24 h on the titanium disks. The adhered tissue sections were then mechanically detached by agitating the culture dishes. The tissue sections remained adherent for significantly longer (15.5 h) on the UV-treated disks than on the untreated control disks (7.5 h). A total of 94% of the tissue sections were adherent for 5 h or longer on the UV-treated disks, whereas only 50% of the sections remained on the control disks for 5 h. The adhesion strength of the tissue sections to the titanium disks, as measured by tensile testing, was six times greater after UV treatment. In the culture studies, mucosal fibroblasts extracted from rat palates were attached to titanium disks by incubating for 24, 48, or 96 h. The number of attached cells was consistently 15–30% greater on the UV-treated disks than on the control disks. The cells were then subjected to mechanical or chemical (trypsinization) detachment. After mechanical detachment, the residual cell rates on the UV-treated surfaces after 24 and 48 h of incubation were 35% and 25% higher, respectively, than those on the control surfaces. The remaining rate after chemical detachment was 74% on the control surface and 88% on the UV-treated surface for the cells cultured for 48 h. These trends were also confirmed in mouse embryonic fibroblasts, with an intense expression of vinculin, a focal adhesion protein, on the UV-treated disks even after detachment. The UV-treated titanium was superhydrophilic, whereas the control titanium was hydrophobic. X-ray photoelectron spectroscopy (XPS) chemical analysis revealed that the amount of carbon at the surface was significantly reduced after UV treatment, while the amount of TiOH molecules was increased. These ex vivo and in vitro results indicate that the UV treatment of titanium increases the adhesion and retention of oral mucosa connective tissue as a result of increased resistance of constituent fibroblasts against exogenous detachment, both mechanically and chemically, as well as UV-induced physicochemical changes of the titanium surface.