There is accumulating evidence that strontium-containing biomaterials have positive effects on bone tissue repair. We investigated the in vitro effect of a new Sr-doped bioactive glass manufactured by the sol-gel method on osteoblast viability and differentiation. Osteoblasts isolated from foetal mouse calvaria were cultured in the presence of bioactive glass particles; particles were undoped (B75) or Sr-doped with 1 wt.% (B75-Sr1) and 5 wt.% (B75-Sr5). Morphological analysis was carried out by contrast-phase microscopy and scanning electron microscopy (SEM). Cell viability was evaluated by the MTS assay at 24 h, 48 h and 72 h. At 24 h, day 6 and day 12, osteoblast differentiation was evaluated by assaying alkaline phosphatase (ALP) activity, osteocalcin (OC) secretion and gene expression of various bone markers, using Real-Time-PCR. Alizarin Red staining and ALP histoenzymatic localisation were performed on day 12. Microscopic observations and MTS showed an absence of cytotoxicity in the three investigated bioactive glasses. B75-Sr5 particles in cell cultures, in comparison with those of B75 and B75-Sr1, resulted in a significant up-regulation of Runx2, Osterix, Dlx5, collagen I, ALP, bone sialoprotein (BSP) and OC mRNA levels on day 12, which was associated with an increase of ALP activity on day 6 and OC secretion on day 12. In conclusion, osteoblast differentiation of foetal mouse calvarial cells was enhanced in the presence of bioactive glass particles containing 5 wt.% strontium. Thus, B75-Sr5 may represent a promising bone-grafting material for bone regeneration procedures.

Cu-doped 45S5 bioactive glasses with varying Cu contents were fabricated and used to process 3D porous scaffolds via the foam replica technique. Cu-doping results in the weakening of the glass network and a decrease in its glass transition temperature. Acellular in vitro studies revealed very high bioactivity independent of Cu doping as indicated by the fast formation of a carbonated hydroxyapatite layer (CHA) on scaffold surfaces after immersion in simulated body fluid (SBF). The kinetics of the glass-ceramic scaffold's transition to an amorphous calcium phosphate layer (ACP) and the crystallisation of CHA were explored by FT-IR and SEM analyses. The elemental distribution in the scaffold/fluid interface region was monitored by the advanced micro-PIXE-RBS (particle induced X-ray emission/Rutherford backscattering spectrometry) method. Cu-containing glasses showed slower release of Si, Ca and P from the scaffold periphery, whereas traces of Cu were found incorporated in the CaP layer on the scaffold surface. Cu release kinetics from the scaffolds in SBF were found to depend on culturing conditions while highest Cu concentrations of ∼3.1 ppm and ∼4.6 ppm under static and quasi-dynamic conditions, respectively, were observed. Since Cu exhibits potential angiogenic and osteogenic properties, the Cu-containing scaffolds are suggested as promising materials for bone tissue engineering applications.

The development of bone tissue regeneration calls for biomaterials able to release biologically active substances in a controlled manner after implantation. In this context, strontium-doped bioactive glasses are of major interest; their key property relies on the increased kinetics of surface reactions, along with the release of critical concentrations of ionic dissolution products capable of stimulating cellular responses. In this paper, we report a complete evaluation of the in vitro reactivity of new SiO₂–CaO–SrO and SiO₂–CaO–P₂O₅–SrO bioactive glasses. In contact with simulated acellular physiological fluids, these materials induce the formation of a calcium phosphate surface layer that closely resembles to the biological apatite present in bones. The two most commonly used materials shapes for clinical applications – glass particles and glass bulk – were studied and provide us with concordant results. Compared to strontium-free materials, the dissolution of SiO₂–CaO–SrO and SiO₂–CaO–P₂O₅–SrO glasses is reduced. However, the surface layer is more quickly transformed into a bone-like apatite phase, according to the kinetics of evolution of the Ca/P atomic ratio. Evidences of the presence of Sr at the glass/biological fluids interface were obtained, along with the demonstration that this element is released in physiological concentrations into the biological environment. Knowing the well-recognized beneficial effects of strontium on cell activity and bone remodeling, this crucial result gives high hopes for the development of innovative applications based on Sr-doped glasses in the treatment of osteoporosis and tissue engineering.

Different sol–gel strategies based on the Stöber method are proposed enabling preparation of nanoparticles of SiO₂–CaO bioactive glass with different size, narrow size distribution and good dispersion capability. Eu³⁺-doped glass nanoparticles with luminescent properties can also be obtained.