A humidity sensor is a crucial device in daily life; therefore, in the present study, a novel humidity sensor was designed to increase its specific surface area to improve its humid sensing capacity and conductivity. Titanium dioxide nanoparticles (TiNP) consisting of zero-dimensional nanospheres and one-dimensional nanotubes were prepared by anodic oxidation. Rod-shaped cellulose nanocrystals (CNCs) with average length and diameter of 60 nm and 800 nm, respectively, were obtained by enzymatic hydrolysis and high pressure homogenization. TiNP/CNC composite films exhibited superior hydrophilicity and large specific surface areas based on Fourier transform infrared spectroscopy and nitrogen adsorption–desorption results. The humidity sensing characteristics of sensors based on TiNP/CNC flexible composite films with varying contents of TiNP were investigated under a relative humidity range of 11–97%. The 6% TiNP/CNC-based humidity sensor exhibited high humidity response, rapid response/recovery speed, and high stability. Furthermore, the humidity sensing mechanism of TiNP/CNC composite films was analyzed based on the density functional theory. TiNP/CNC-based humidity sensors could be applied in flexible and wearable electronics.

An oxygen-enhanced organosolv fractionation method to produce lignin from waste biomass was investigated. In this novel biorefinery process, mild conditions, i.e., temperature at 80 to 100 °C and pressure < 0.8 MPa, were employed to alleviate energy input and to retain the original lignin structure as much as possible. The results showed that the lignin yield was increased with increasing process temperature, ethanol concentration, and ratio of liquid to solid. Although little structural changes were observed, the normalized Infrared transmittance results revealed quantitative differences. Moreover, a basic kinetic study was conducted, and the results showed that there existed two stages with fast and slow rates during the delignification processes. Analysis of the fibers’ micro-structure also demonstrated the effectiveness of oxygen-enhanced organosolv fractionation. However, a phenol-based inducer could possibly further improve the efficiency based on the delignification mechanism of reactive oxygen species, which will be studied in future research.