Monolithical series connection of silicon thin-film solar cells modules performed by laser scribing plays a very important role in the entire production of these devices. In the current laser process interconnection the two last steps are developed for a configuration of modules where the glass is essential as transparent substrate. In addition, the change of wavelength in the employed laser sources is sometimes enforced due to the nature of the different materials of the multilayer structure which make up the device. The aim of this work is to characterize the laser patterning involved in the monolithic interconnection process in a different configurations of processing than the usually performed with visible laser sources. To carry out this study, we use nanosecond and picosecond laser sources working at 355 nm of wavelength in order to achieve the selective ablation of the material from the film side. To assess this selective removal of material has been used EDX (energy dispersive using X-ray) analysis, electrical measurements and confocal profiles. In order to evaluate the damage in the silicon layer, Raman spectroscopy has been used for the last laser process step. Raman spectra gives information about the heat affected zone in the amorphous silicon structure through the crystalline fraction calculation. The use of ultrafast sources, such as picoseconds lasers, coupled with UV wavelength gives the possibility to consider materials and substrates different than currently used, making the process more efficient and easy to implement in production lines. This approach with UV laser sources working from the film side offers no restriction in the choice of materials which make up the devices and the possibility to opt for opaque substrates.

Lasers have advantages as bone surgical tools over mechanical methods, but two goals should be achieved to assure its use: Similar ablation rates to those obtained with mechanical tools (1 mm³/s at least) and to avoid thermal damage, a condition that can prevent proper bone healing. We present results of cow femoral bone with a 355 nm nanosecond (ns) and a 1064 nm picosecond (ps) pulsed laser sources that allow us to discuss the influence on the process of pulse duration and the selective ablation through high energy absorption (as bone highly absorbs 355 nm radiation). The treated samples were characterized by scanning electron microscopy (SEM) and Raman spectroscopy. The evaluation of the thermal effects produced in the samples shows clear differences between both laser sources: On one hand, the ns laser allows reaching high ablation rates (around 1 mm³/s); Raman spectra show no signal of bone carbonization, but unavoidable thermal effects in the form of melted and solidified material have been observed by electron microscopy in the samples treated with this laser. On the other hand, ablation without any sign of thermal effects is obtained using the ps laser, but with lower ablation rates, (around 0.15 mm³/s).