Nanoparticles were proposed as antibacterial cement admixtures for the production of cement-based composites. Nevertheless, the standards for evaluation of such admixtures still do not indicate which model organisms to use, particularly in regard to the further application of material. Apart from the known toxicity of nanomaterials, in the case of cement-based composites there are limitations associated with the mixing and dispersion of nanomaterials. Therefore, four nanooxides (Al₂O₃, CuO, Fe₃O₄, and ZnO) and seven microorganisms were tested to initially evaluate the applicability of nanooxides in relation to their further use in cement-based composites. Studies of nanoparticles included chemical analysis, microbial growth kinetics, 4- and 24 h toxicity, and biofilm formation assay. Nanooxides showed toxicity against microorganisms in the used concentration, although the populations were able to re-grow. Furthermore, the effect of action was variable even between strains from the same genus. The effect of nanoparticles on biofilms depended on the used strain. Gathered results show several problems that can occur while studying nanoparticles for specific further application. Proper protocols for nanomaterial dispersion prior the preparation of cement-based composites, as well as a standardized approach for their testing, are the fundamental issues that have to be resolved to produce efficient composites.

In the last decade, nanotechnology has been gathering a spectacular amount of attention in the field of building materials. The incorporation of nanosized particles in a small amount to the building materials can influence their properties significantly. And it can contribute to the creation of novel and sustainable structures. In this work, the effect of nano-Fe3O4 as an admixture (from 1 to 5 wt.% in mass of the cement) on the mechanical and microstructural properties of cementitious composites has been characterised. The study showed that Fe3O4 nanoparticles acted as a filler which improved the microstructure of a cementitious composite and reduced its total porosity, thus increasing the density of the composite. The presence of nanomagnetite did not affect the main hydration products and the rate of cement hydration. In addition, the samples containing nanomagnetite exhibited compressive strength improvement (up to 20 %). The study showed that 3 wt.% of nano-Fe3O4 in the cementitious composite was the optimal amount to improve both its mechanical and microstructural properties.

Exposure to elevated temperatures has detrimental effects on the properties of cementitious composites, leading to irreversible changes, up to total failure. Various methods have been used to suppress the deterioration of concrete under elevated temperature conditions. Recently, nanomaterials have been introduced as admixtures, which decrease the thermal degradation of cement-based composites after exposure to high temperatures. This paper presents a comprehensive review of recent developments related to the effects of nanoparticles on the thermal resistance of cementitious composites. The review provides an updated report on the effects of temperature on the properties of cement-based composites, as well as a detailed analysis of the available literature regarding the inclusion of nanomaterials and their effects on the thermal degradation of cementitious composites. The data from the studies reviewed indicate that the inclusion of nanoparticles in composites protects from strength loss, as well as contributing to a decrease in disruptive cracking, after thermal exposure. From all the nanomaterials presented, nanosilica has been studied the most extensively. However, there are other nanomaterials, such as carbon nanotubes, graphene oxide, nanoclays, nanoalumina or nano-iron oxides, that can be used to produce heat-resistant cementitious composites. Based on the data available, it can be concluded that the effects of nanomaterials have not been fully explored and that further investigations are required, so as to successfully utilize them in the production of heat-resistant cementitious composites.