We report on the observation of a fine structure in ion tracks in amorphous ${\mathrm{SiO}}_2$ using small angle x-ray scattering measurements. Tracks were generated by high energy ion irradiation with Au and Xe between 27 MeV and 1.43 GeV. In agreement with molecular dynamics simulations, the tracks consist of a core characterized by a significant density deficit compared to unirradiated material, surrounded by a high density shell. The structure is consistent with a frozen-in pressure wave originating from the center of the ion track as a result of a thermal spike.

Swift heavy-ion irradiation of elemental metal nanoparticles (NPs) embedded in amorphous SiO2 induces a spherical to rodlike shape transformation with the direction of NP elongation aligned to that of the incident ion. Large, once-spherical NPs become progressively more rodlike while small NPs below a critical diameter do not elongate but dissolve in the matrix. We examine this shape transformation for ten metals under a common irradiation condition to achieve mechanistic insight into the transformation process. Subtle differences are apparent including the saturation of the elongated NP width at a minimum sustainable, metal-specific value. Elongated NPs of lesser width are unstable and subject to vaporization. Furthermore, we demonstrate the elongation process is governed by the formation of a molten ion-track in amorphous SiO2 such that upon saturation the elongated NP width never exceeds the molten ion-track diameter.

Pt nanoparticles (NPs) formed by ion-beam synthesis in amorphous ${\text{SiO}}_2$ were irradiated with Au ions in the energy range of 27–185 MeV. Small-angle x-ray scattering (SAXS) and transmission electron microscopy were used to characterize an irradiation-induced shape transformation within the NPs. A simple yet effective way of analyzing the SAXS data to determine both NP dimensions is presented. A transformation from spherical to rodlike shape with increasing irradiation fluence was observed for NPs larger than an energy-dependent threshold diameter, which varied from 4.0 to 6.5 nm over 27–185 MeV. NPs smaller than this threshold diameter remained spherical upon irradiation but decreased in size as a result of dissolution. The latter was more pronounced for the smallest particles. The minor dimension of the transformed NPs saturated at an energy-dependent value comparable to the threshold diameter for elongation. The saturated minor dimension was less than the diameter of the irradiation-induced molten track within the matrix. We demonstrate that Pt NPs of diameter 13 nm reach saturation of the minor dimension beyond a total-energy deposition into the matrix of $20\text{keV}/{\text{nm}}^3$.