The emergence of digital dentistry has led to the introduction of various three-dimensional (3D) printing materials in the market, specifically for provisional fixed restoration. This study aimed to undertake a systematic review of the published literature on the Mechanical Properties of 3D- Printed Provisional Resin Materials for crown and fixed dental prosthesis (FDP). The electronic database on PubMed/Medline was searched for relevant studies. The search retrieved articles that were published from January 2011 to March 2023. The established focus question was: “Do provisional 3D-printed materials have better mechanical properties than conventional or milled provisional materials?”. The systematically extracted data included the researcher’s name(s), publication year, evaluation method, number of samples, types of materials, and study outcome. A total of 19 studies were included in this systematic review. These studies examined different aspects of the mechanical properties of 3D-printed provisional materials. Flexural Strength and Microhardness were the frequently used mechanical testing. Furthermore, 3D-printed provisional restorations showed higher hardness, smoother surfaces, less wear volume loss, and higher wear resistance compared to either milled or conventional, or both. 3D-printed provisional resin materials appear to be a promising option for fabricating provisional crowns and FDPs.

The aim of this study was to evaluate the effect of different cleaning methods on the shear bond strength (SBS) of resin cement to contaminated zirconia specimens. Eighty rectangular-shaped specimens (2 × 5 × 10 mm) were fabricated from Zirconia blocks (IPS e.max ZirCAD) and randomly divided into 8 groups (n = 10). Group A (control) was not exposed to contaminants. The following tests specimens were contaminated with saliva and silicone indicating paste. Group B was coated with ceramic primer, then subjected to contamination. Groups C, D, E, F, G, and H were contaminated; cleaned with water rinse, Ivoclean, air particle abrasion, hydrofluoric acid, KATANA^TM Cleaner and ZirClean^TM, respectively, and then coated with ceramic primer and bonded to dual cure resin cement cylinders. All the specimens were subjected to artificial aging and surviving specimens were subjected to the SBS test. For statistical analysis, ANOVA and multiple comparison methods at the 0.05 significance level were used. There was no statistically significant difference among Ivoclean (21.48 ± 2.90 MPa), air particle abrasion (21.92 ± 2.85 MPa), and the control group (24.68 ± 5.46). The application of ceramic primer before contamination did not preserve the SBS of resin cement to zirconia. Cleaning the contaminated zirconia surface with hydrofluoric acid (15.03 ± 3.63) or KATANA^TM Cleaner (17.27 ± 7.63) did not restore SBS to the uncontaminated state, but it was significantly higher than simply rinsing with water (12.46 ± 5.17) or the use of ZirClean^TM (11.59 ± 5.53). The bond strength of resin cement to zirconia was influenced by cleaning methods.

This in vitro study aimed to evaluate the fracture resistance and mode of failure of endocrowns with proximal extension design compared to the conventional design, and to assess the agreement of evaluators on the failure mode. Twenty mandibular third molars free of caries with approximately similar root lengths and crown dimensions were sectioned parallel to the occlusal plane 2 mm above the cementoenamel junction (CEJ). Then, pulp chambers and canals were accessed, cleaned, and smoothed for the path of insertion. To achieve a symmetrical pulp chamber with an average depth of 3 mm, chambers were filled with flowable resin composite. Then, teeth were randomly divided into two groups (n = 10). The control group has all the walls at the same level. The test group had a box extension on the proximal wall 2 mm apical to the buccal and lingual wall level. Endocrowns (n = 20) of two different designs (conventional and proximal extensions) were fabricated using lithium disilicate (IPS e.max CAD, Ivoclar Vivadent, Schaan, Liechtenstein). After cementation, specimens were loaded with a round-end vertical loading tip at a rate of 0.5 mm per minute until fracture (INSTRON, Norwood, MA, USA). Then, the fractured specimens were collected for evaluation and assessment. Statistical analyses were performed using the Mann-Whitney U-test (α = 0.05) for fracture test analysis and Cohen’s Kappa for inter-rater reliability. The Mann-Whitney U-test showed a non-significant difference between the two groups (p = 0.142). However, the mode of failure of the endocrown with proximal extension showed more catastrophic failures than the conventional design. Adding proximal boxes to the endocrown design did not negatively impact the fracture resistance of the restoration. Visualization of the fracture line and tracing their apical end by direct vision or other diagnostic tools is an essential part of the evaluation of failures of endocrowns. Endodontically treated molar teeth with proximal caries extension might be restored with an endocrown with proximal extension. Clinicians should take extra care when visualizing the fracture lines and tracing their apical end as it might be very misleading.

The aim of this study was to investigate the effect of repeated pressing of lithium disilicate ceramic on the shear bond strength (SBS) of three types of resin cement. Methodology: A lithium disilicate ceramic (IPS e.max^® Press) was first heat-pressed to form rectangular disk specimens. Then, leftovers were used for the second and third presses. A total of 90 specimens were prepared and separated, according to the number of pressing cycles, into three groups: 1st, 2nd, and 3rd presses (n = 30). Each group was further subdivided into three groups (n = 10) according to the type of resin cement used, as follows: Multilink N (MN), Variolink Esthetic DC (VDC), and Variolink Esthetic LC (VLC). All the cement was bonded to the ceramic surface, which was etched with hydrofluoric acid and primed with Monobond Plus. All samples were light-cured and stored for 24 h. Shear bond strength was tested on a universal testing machine. Results: A two-way ANOVA was used to evaluate the influence of repeated pressing cycles and cement type as well as their interaction. The results indicated that cement type has a significant impact (p < 0.001) but not the number of pressing cycles (p = 0.970) or their interaction (p = 0.836). The Bonferroni post-hoc test showed that the SBS of MN was significantly higher than that of VDC and VLC in the first press and second press cycles, respectively. The SBS of MN was significantly higher than that of VDC and VLC cements in the third pressing cycle. There was no significant difference in the SBS between VLC and VDC in all three pressing cycles. Conclusion: The results of the current study did not report a detrimental effect of repeated pressing up to three cycles on the shear bond strength of the IPS e.max^® Press. Multilink resin cement showed the highest SBS to IPS e.max^® Press at the third pressing cycle. For all types of cement and heat pressing cycles, the majority of cement failures were adhesive. No cohesive failures occurred in any of the tested resin cements, regardless of the cement type or the number of heat pressing cycles tested.

Effect of Dentin Contamination with Hemostatic Agents and Cleaning Techniques on Bonding with Self-Adhesive Resin Cement - Article abstract #943353