Alumina ceramics with different sintering temperatures in argon atmosphere were obtained using stereolithography-based 3D printing. The effects of sintering temperature on microstructure and physical and mechanical properties were investigated. The results show that the average particle size, shrinkage, bulk density, crystallite size, flexural strength, Vickers hardness, and nanoindentation hardness increased with the increase in sintering temperature, whereas the open porosity decreased with increasing sintering temperature. No change was observed in phase composition, chemical bond, atomic ratio, and surface roughness. For the sintered samples, the shrinkage in Z direction is much greater than that in X or Y direction. The optimum sintering temperature in argon atmosphere is 1350 °C with a shrinkage of 3.0%, 3.2%, and 5.5% in X, Y, and Z directions, respectively, flexural strength of 26.7 MPa, Vickers hardness of 198.5 HV, nanoindentation hardness of 33.1 GPa, bulk density of 2.5 g/cm3, and open porosity of 33.8%. The optimum sintering temperature was 70 °C higher than that sintering in air atmosphere when achieved the similar properties.

In this work, alumina ceramics were formed via stereolithography-based 3D printing technology in order to fabricate ceramic cores in a fast and cost-effective way. Effects of holding time during sintering on microstructure and properties of alumina ceramics were investigated. Sintered alumina ceramics were made up of layered structures due to layer-by-layer forming method. In addition, interlayer spacing decreased with the increase in holding time. Average particle size, shrinkage, crystallite size, flexural strength, and hardness increased with the increase in holding time due to strong interfacial bonding among alumina particles. Open porosity decreased slightly as holding time increased. Moreover, it was found that holding time had little influence on bulk density, phase composition, and chemical bonds of the ceramics. The shrinkage in Z direction was about 1.8 times higher than that in X or Y directions due to layered structure caused by 3D printing forming method. The optimum holding time was 90 min, which resulted in ceramics with interlayering spacing of 11.8 μm, shrinkage of 2.1% in X direction, 2.1% in Y direction, and 4.1% in Z direction, flexural strength of 20.7 MPa, nano-indentation hardness of 17.6 GPa, Vickers hardness of 114.3 HV, bulk density of 2.5 g/cm³, and open porosity of 39.0%.