Experimental data on the effect of grain sizes on the shape and width of the hysteresis loop characterizing a metal-semiconductor phase transition in vanadium dioxide films are analyzed in terms of the classical theory of nucleation. It is shown that the factors responsible for the changes in the shape and width of the hysteresis loop with variations in the size of the grains making up a film are associated with the heterogeneous character of nucleation of a new phase, on the one hand, and with the elastic stresses arising in the phase transition, on the other.

Hydrogen penetration into thin films of vanadium dioxide from aqueous solutions of mono-, di-, and tribasic alcohols is studied. It is shown that this process is reversible, has a catalytic character, and brings about a lowering of the metal-semiconductor phase transition temperature. It is established that the phase transition in a hydrogenated H_xVO₂ film is completely suppressed for x> 0.04.

Polyvinylidene fluoride and its co-polymer with trifluoroethylene are promising biomaterials for supporting nerve regeneration processes because of their proven biocompatibility and piezoelectric properties that could stimulate cell ingrowth due to electrical activity upon mechanical deformation. This study reports the piezoelectric effect of electrospun polyvinylidene fluoride scaffolds in response to mechanical loading. An impact test machine was used to evaluate the generation of electrical voltage upon application of an impact load. Scaffolds were produced via electrospinning from polyvinylidene fluoride and polyvinylidene fluoride-co-trifluoroethylene with concentrations of 10–20 wt% dissolved in N,N-dimethylformamide (DMF) and acetone (6:4). The structural and thermal properties of scaffolds were analyzed using Fourier Transform Infrared Spectroscopy and Differential Scanning Calorimetry, respectively. The piezoelectric response of the scaffolds was induced using a custom-made manual impact press machine. Impact forces between 0.4 and 14 N were applied. Fourier Transform Infrared Spectroscopy and Differential Scanning Calorimetry results demonstrated the piezoelectric effect of the electrospun polyvinylidene fluoride and polyvinylidene fluoride-co-trifluoroethylene scaffolds. All the scaffolds exhibited a piezoelectric polar beta-phase formation. Their thermal enthalpies were higher than the value of the initial materials and exhibited a better tendency of crystallization. The electrospun scaffolds exhibited piezoelectric responses in form of voltage by applying impact load. Polyvinylidene fluoride-co-trifluoroethylene scaffolds showed higher values in the range of 6–30 V as compared to pure polyvinylidene fluoride. Here, the mechanically induced electrical impulses measured were between 2.5 and 8 V. Increasing the impact forces did not increase the piezoelectric effect. The results demonstrate the possibility of producing electrospun polyvinylidene fluoride and polyvinylidene fluoride-co-trifluoroethylene scaffolds as nerve guidance with piezoelectric response. Further experiments must be carried out to analyze the piezoelectricity at dynamic conditions.

Tissue engineering and cell-based therapy approaches require artificial scaffolds as extracellular matrix (ECM) and three-dimensional (3D) environment for clinically relevant cells to attach, be metabolically active and proliferate. Moreover, these constructs must possess mechanical and physical-chemical properties matched with certain implantation site. If all the required conditions are met, a tissue-engineered construct is considered as functional and will regenerate or replace the damaged tissue after implantation. In this work, we give a short overview of so-called electrohydrodynamic approach (EHD), e.g. with an application of electric field, to fabricate nano- and microstructured porous polymeric networks. This includes the application of electrospinning (networks) and electrospraying (micro- and macrospheres) to produce scaffolds and semipermeable hydrogel structures as a basis for tissue engineering and cell-based therapies.

Dielectric properties of polyvinylidene fluoride based thin films and electrospun mats have been studied. Frequency dependences of samples capacity and tangent of dielectric losses have been obtained. The influence of trifluoroethylene presence in copolymer on dielectric properties has been investigated. Efficiency of using deposited contacts instead of pressed contacts was considered.

It is shown that the method for the growth of conducting polyaniline nanotubes, based on the direct polymerization of aniline on the surface of channels in track membranes, can be used to produce...