In this paper, laser surface treatment of Al alloy was studied by comparison of sandblasting and laser ablation. The effects of laser spot distribution on surface roughness, contact angle, chemical composition and shear strength of Al alloy were analyzed. The experimental results showed that the bonding performance of Al alloy are promoted by controlling the laser spot spacing. When laser spot spacing was smaller than the size of the laser spot, micro–nano composite structures were induced by multiple laser pulses, which would improve shear strength by increasing the contact area between Al alloy and adhesive. Using laser surface treatment, the adhesion properties on Al alloy can be promoted.

Lithium niobate (LiNbO₃) has become popular with applications in electronics and communication industries due to its excellent electro-optical and nonlinear properties. This paper presents the influence of laser power, repetition frequency, number of subpulses, depth of each pass, and scanning velocity in picosecond laser dicing on multiple characteristics of LiNbO₃ using the Taguchi method. By means of analysis of variance and analysis of relations between the characteristics, the optimal ps-laser-dicing parameter is obtained with good quality and high efficiency, which is applied to LiNbO₃ products. The result indicates that picosecond laser dicing provides an alternative to machine thick LiNbO₃ wafers with narrow kerf width, micro chipping, smooth surface, and high productivity.

The disabled glue on valve surfaces is known to reduce aircraft durability and performance. In this paper, glue contaminants were removed from 2Cr13 stainless valves by dry-type laser processing with a cold air gun and compared with the chemical soaking method. The laser-processed surface was examined by white-light interferometer, scanning electron microscopy, energy dispersive spectroscopy, X-ray diffractometer, hardness tester, and metallographic microscopy. The substrate surface became a little smoother but also had deeper dips due to laser thermal melting. After laser degumming, the new constituent was found in the laser-irradiated region and analyzed as FeCr_0.29Ni_0.16C_0.06, since the ratio of chemical compositions changed. Based on our simulation and experiments, the temperature of the workpiece was effectively controlled by the cold air gun, and its physical properties, including hardness and metallographic structure, were hardly changed. It was shown that laser degumming provides an alternative method for metal valve cleaning.