Two polymorphs of tolazamide, N-[(azepan-1-ylamino)carbonyl]-4-methylbenzenesulfonamide, a sulfonylurea anti-diabetic drug, have different densities and molecular packings. Polymorph II converts into polymorph I in the solid state on heating or via recrystallization if solvent-assisted. The effect of pressure on the two forms and the possibility of a transformation to a denser form on compression have been studied. No phase transitions have been observed in either of the forms in a pentane–isopentane mixture (when no recrystallization is possible). Polymorph II recrystallized partly into a denser polymorph I in methanol at 0.1 GPa, but the transformation stopped at an early stage. Solid state DFT calculations of the two forms as well as conformational landscape investigation in the gas phase were used to rationalize this result. The anisotropic pressure-induced strain of the two polymorphs has been compared in relation to changes in the hydrogen bond geometry and the behavior of stacking interactions.

Bimetallic nanoparticles expand the possibilities of catalyst design, providing an extra degree of freedom for tailoring the catalyst structure in comparison to purely monometallic systems. The distribution mode of two metal species defines the structure of surface catalytic sites, and current research efforts are focused on the development of methods for their controlled tuning. In light of this, a comprehensive investigation of the factors which influence the changes in the morphology of bimetallic nanoparticles, including the elemental redistribution, are mandatory for each particular bimetallic system. Here we present the combined XPS/STM study of the surface structure and morphology of bimetallic Pt-Au/HOPG nanoparticles prepared by thermal vacuum deposition and show that thermal annealing up to 350 °C induces the alloying process between the two bulk-immiscible metal components. Increasing the treatment temperature enhances the extent of Pt-Au alloying. However, the sintering of nanoparticles starts to occur above 500 °C. The approach implemented in this work includes the theoretical simulation of XPS signal intensities for a more meticulous analysis of the compositional distribution and can be helpful from a methodological perspective for other XPS/STM studies of bimetallic nanoparticles on planar supports.

Copper nanoparticles supported on alumina have been synthesized from CuAl-layered double hydroxide and have been studied in methanol oxidation at different molar ratios of the components of the reaction feed by in situ XPS and mass-spectrometry.

In this study, the dependence of the catalytic activity of highly oriented pyrolytic graphite (HOPG)-supported bimetallic Pd-Au catalysts towards the CO oxidation based on the Pd/Au atomic ratio was investigated. The activities of two model catalysts differing from each other in the initial Pd/Au atomic ratios appeared as distinctly different in terms of their ignition temperatures. More specifically, the PdAu-2 sample with a lower Pd/Au surface ratio (~0.75) was already active at temperatures less than 150 °C, while the PdAu-1 sample with a higher Pd/Au surface ratio (~1.0) became active only at temperatures above 200 °C. NAP XPS revealed that the exposure of the catalysts to a reaction mixture at RT induces the palladium surface segregation accompanied by an enrichment of the near-surface regions of the two-component Pd-Au alloy nanoparticles with Pd due to adsorption of CO on palladium atoms. The segregation extent depends on the initial Pd/Au surface ratio. The difference in activity between these two catalysts is determined by the presence or higher concentration of specific active Pd sites on the surface of bimetallic particles, i.e., by the ensemble effect. Upon cooling the sample down to room temperature, the reverse redistribution of the atomic composition within near-surface regions occurs, which switches the catalyst back into inactive state. This observation strongly suggests that the optimum active sites emerge under reaction conditions exclusively, involving both high temperature and a reactive atmosphere.