The influence of Si, Cu, B, and trace alloying elements on the conductivity of aluminum die cast 12 (ADC12) alloy was investigated. The conductivity decreased linearly with increasing volume fraction of the Si phase attributed to a linear decrease of the volume of the more conductive Al phase through a rule of mixtures. The conductivity also decreased with increasing Cu content, between 0~3%. The conductivity increased with increasing B content, reached the peak at 0.02% B and thereafter decreased somewhat. The mechanism was that B reacted with the transition element in the Al phase to form boride, decreasing the transition element concentration in the Al lattice, and decreasing the lattice constant. The thermal conductivity, λ, was related to the electrical conductivity, $\sigma$, by means of $\mathsf{\lambda }=\mathrm{LT}\mathsf{\sigma }+{\mathsf{\lambda }}_{\mathrm{g}}$, where L is the apparent Lorentz constant, 1.86 × 10⁻⁸; T is the absolute temperature, 293 K; λ_g is the lattice conductivity, 42.3 W/(m·K).

For biodegradable pure iron implants, a higher biodegradation rate is preferred. In this work, we compared the biodegradation of pure iron prepared by microwave sintering and laser melting (designated as MSed Fe and LMed Fe, respectively). The MSed Fe presented a distinct porous structure, while the LMed Fe presented a relatively compact structure without any obvious pores. The biodegradation rate of the MSed Fe was higher than that of the LMed Fe, and their biodegradation rates were higher than that of the as-cast Fe. The biodegradation rates of the MSed Fe and the LMed Fe were approximately 44 and 13 times higher than that of the as cast Fe, respectively. The biodegradation was closely related to the microstructure’s compactness and grain size. Moreover, the MSed Fe and the LMed Fe had satisfactory biocompatibility.