Superabsorbent polymers (SAPs) are crosslinked hydrophilic polymers that are capable of absorbing large amounts of water. Commercial SAPs are mostly produced with acrylic acid that cannot be easily biodegraded. Therefore, in this study, polysaccharide-based SAPs using carboxymethyl cellulose as a major component were prepared. Starch aldehydes and citric acid were selected due to their environment-friendly, non-toxic, and biodegradable properties compared to conventional crosslinking agents. Starch aldehydes were prepared by periodate oxidation, which forms aldehyde groups by taking the places of C–OH groups at C-2 and C-3. Furthermore, starch aldehydes were analyzed through the change in FT-IR spectra, the aldehyde quantitation, and the morphology in FE-SEM images. In the crosslinking of polysaccharide-based SAPs, the acetal bridges from starch aldehydes led to a large amount of water entering the network structure of the SAPs. However, the ester bridges from citric acid interfered with the water penetration. In addition, the swelling behavior of the SAPs was analyzed by the Fickian diffusion model and the Schott’s pseudo second order kinetics model. The relationship between swelling behavior and morphology of the SAPs was analyzed by FE-SEM images. In conclusion, polysaccharide-based SAPs were well prepared and the highest equilibrium swelling ratio was 87.0 g/g.

The purpose of this study is to modify lignin for better blending with general purpose synthetic polymers. The possible advantages by using this modification would be cost reduction, better physical properties, and biodegradability. In this study, butyrolactone-modified lignin (BLL) and tetrahydrofuran-modified lignin (THFL) were used for aliphatic chain modification of lignin using an acid-catalyzed esterification method in order to mimic the relation of lignin-carbohydrate-complex (LCC) and cellulose. The results of several analyses indicated that lignin was well modified. It was confirmed that the lignin was modified as expected and the reaction sites of the modification, as well as the reaction behaviors, were varied by the reagent types. The result of X-ray diffraction analysis (XRD) analysis indicated that modified lignin/polymer blends increased the crystallinity due to their good compatibility. It can be confirmed that the type of alkyl chain and the miscibility gap between the alkyl chain-matrix affected the mechanical properties enormously in the fungi-degradable environment. From this study, a new method of lignin modification is proposed, and it is found that modified lignin retains the property of the substituted aliphatic chain well. This method could be a proper lignin modification method.