Integrating superior mechanical performance, anisotropic conductivity, and biocompatibility into conductive hydrogels as all‐in‐one human‐machine interaction device remains challenging. Herein, by mimicking the anisotropic structures of human muscles, a robust anisotropic conductive hydrogel is developed by initially aligning polyvinyl alcohol with polypyrrole decorated cellulose nanofibrils to form an anisotropically oriented polymer networks, followed by post‐crosslinking with tannic acid (TA). Introducing TA into hydrogel network permanently secures its hierarchically anisotropic structure through multiple hydrogen bonds, thus endowing the hydrogel with exceptional mechanical properties (tensile strength of 11.41 MPa, toughness of 12.44 MJ m⁻³), anisotropic adhesive property, and direction‐dependent conductivity. With these attributes, a hydrogel strain sensor with excellent multidirectional sensitivity is developed, enabling stable monitoring of multi‐degrees of freedom joint movements in the human body and facilitating the control of a multiaxial virtual robot manipulator. Moreover, the in vitro/vivo tests demonstrate exceptional biocompatibility and anti‐biofouling properties of the as‐prepared hydrogel sensor, maintaining stable electronic response signals for over 14 days after successful implantation into the Achilles tendon of mice. Overall, this study presents a promising approach for designing conductive hydrogels with superior mechanical properties and anisotropic functionality for emerging applications in both in vitro and in vivo human‐machine interface materials.

To develop green efficient anti-corrosion coatings, graphene/lacquer composite coatings were demonstrated.

Zwitterionic polymer coatings facilitate the formation of hydration layers via electrostatic interactions on their surfaces and have demonstrated efficacy in preventing biofouling. They have emerged as a promising class of marine antifouling materials. However, designing multifunctional, environmentally friendly, and natural products-derived zwitterionic polymer coatings that simultaneously resist biofouling, inhibit protein adhesion, exhibit strong antibacterial properties, and reduce algal adhesion is a significant challenge. This study employed two diisocyanates as crosslinkers and natural urushiol and ethanolamine as raw materials. The coupling reaction of diisocyanates with hydroxyl groups was employed to synthesize urushiol-based precursors. Subsequently, sulfobetaine moieties were introduced into the urushiol-based precursors, developing two environmentally friendly and high-performance zwitterionic-functionalized polyurushiol antifouling coatings, denoted as HUDM-SB and IPUDM-SB. The sulfobetaine-functionalized polyurushiol coating exhibited significantly enhanced hydrophilicity, with the static water contact angle reduced to less than 60°, and demonstrated excellent resistance to protein adhesion. IPUDM-SB exhibited antibacterial efficacy up to 99.9% against common Gram-negative bacteria (E. coli and V. alginolyticus) and Gram-positive bacteria (S. aureus and Bacillus. sp.). HUDM-SB achieved antibacterial efficacy exceeding 95.0% against four bacterial species. Furthermore, the sulfobetaine moieties on the surfaces of the IPUDM-SB and HUDM-SB coatings effectively inhibited the growth and reproduction of algal cells by preventing microalgae adhesion. This zwitterionic-functionalized polyurushiol coating does not contain antifouling agents, making it a green, environmentally friendly, and high-performance biomaterial-based solution for marine antifouling.

Silver nanoparticle-based coatings have been regarded as promising candidates for marine antifouling. However, current toxic fabrication methods also lead to environment risks. Nanoparticle agglomeration, poor compatibility with polymer, and rapid release of Ag⁺ result in short-term efficacy. In this study, a facile one-pot synthesis method of silver nanoparticles (AgNPs) encapsulated in polymeric urushiol (PUL) was developed. AgNPs were synthesized in situ by natural urushiol, serving as a reductant, dispersant and surfactant. Simultaneously, silver nitrate catalyzed the polymerization of urushiol into PUL. This in situ reduction method made AgNPs uniformly distributed in the polymer matrix. The binding between the AgNPs and the PUL resulted in the stable release of Ag⁺. Results showed the antibacterial rate of a 0.1% AgNPs coating is 100% in laboratory experiments. This environment-friendly coating showed good microbial inhibition performance with long-term (120 days) marine antifouling efficacy. This study shows the potential of preparing an eco-friendly coating with long-term marine antifouling ability.