Formaldehyde-derived wood adhesives have dominated in woody composites production up to now, while facing a significant challenge in non-renewable raw materials and the formaldehyde emission. To solve these problems, an eco-friendly soybean protein-based wood adhesive was explored via the addition of renewable cardanol based epoxy (CBE) as cross-linking agent. The curing mechanism and viscosity of the adhesives were investigated and the bonding performance was evaluated with three-ply plywood. Fourier transformed infrared spectroscopy (FTIR) analysis confirmed the formation of new ether linkages and the consumption of epoxy groups in the cured adhesives, thereby improving the thermal stabilities and cohesion. Plywood bonded with the CBE-modified soybean protein-based adhesive reached the maximum wet shear strength of 1.11 MPa (4 wt.% CBE addition), a 48% increase compared to the control, whereas the viscosity of adhesive decreased by 68.2%. The wet shear strength of the plywood met the requirements of the Chinese National Standard GB/T 9846-2015 for interior plywood application. The formaldehyde-free adhesive with excellent water resistance adhesiveness performance shows great potential in woody composites as an alternative to formaldehyde derived wood adhesives.

With rising interior air pollution, health, and food shortage concerns, wood adhesives derived from non-food sustainable materials have therefore attracted considerable attention. Here we developed an eco-friendly cottonseed-lignin adhesive consisting of non-food defatted cottonseed flour (DCF), alkali lignin (AL), and graphene oxide (GO). The cation-π interaction, and hydrogen and covalent bonds between AL@GO and DCF collectively enhanced the cross-linking structure of the cured cottonseed-lignin adhesive, based on the Fourier-transform infrared spectroscopy, thermogravimetric analyses, scanning electron microscopy, and sol-gel tests. The high performance of the developed cottonseed-lignin adhesive was evidenced by its increased wet/dry shear strength and decreased rheological properties before curing and improved thermal stability and decreased soluble substances after curing. Particularly, the highest wet shear strength of poplar plywood bonded with cottonseed-lignin adhesive was 1.08 MPa, which increased by 74.2 and 54.3% as compared to the control and requirement of the Chinese standard GB/T 9846-2015 for interior plywood (≥0.7 MPa), respectively. The technology and resultant adhesives showed great potential in the preparation of green woody composites for many applications.