Argon oxygen decarbonization (AOD) slag refers to a byproduct of stainless steel (SS) production, which has caused considerable environmental stress. Finding an effective approach for recycling AOD slag is essential to environmental safety. In this work, batch leaching tests were carried out to explore the leaching behavior of AOD slag and soil. Pot experiments was conducted to analyze the fertilization effect of AOD slag for tall fescue (Festuca arundinacea Schreb) planting. The plant height, biomass, total root length (TRL), root surface area (RSA), root tips (RT), root hairs (RH)), chlorophyll content, malondialdehyde (MDA) content, and antioxidant enzyme activities of the tall fescue seedlings were measured. As indicated from the results, adding AOD slag into soil increased soil pH. The leaching concentration of Ca, Si, Al, Cr of the AOD slag was higher than the original soil, while that of Mg, Mn, and Fe was lower. Low addition rate (≤1%) of AOD slag fertilization was good for plant height, biomass, root growth, and chlorophyll synthesis, whereas high addition rate (≥2%) exerted an opposite effect. Elevating the rate of AOD slag fertilization increased the Cr accumulation in the tall fescue seedling that aggravated damage of reactive oxygen species (ROS). When the AOD slag fertilization was at a low rate (≤1%), ROS scavenging was attributed to the synergistic effects of superoxide dismutase (SOD), peroxidase (POD), and catalase (CAT) defense systems, while at a high rate (≥2%) of AOD slag fertilization, scavenging of excessive ROS could be mainly due to the CAT defense system.

Argon oxygen decarburization (AOD) slag is the by-product of the stainless steel refining process, which has caused considerable environmental stress. In this work, the utilization of AOD slag as mineral fertilizer for alfalfa (Medicago sativa L.) and perennial ryegrass (Lolium perenne L.) planting were investigated by pot experiments. The morpho-physiological parameters of biomass, plant height, root morphology and the biochemical parameters of malondialdehyde (MDA) content, superoxide dismutase (SOD) activity, catalase (CAT) activity, peroxidase (POD) activity, and chlorophyll were measured. The accumulation of chromium in plants was also determined for an environmental safety perspective. It was found that low rates (≤0.5 wt.% for alfalfa and ≤2 wt.% for perennial ryegrass) of AOD slag fertilization are beneficial to the growth of these two plants. However, the soil enrichment with higher AOD slag amounts resulted in the reduction of biomass, plant height, and root growth. Compared with the alfalfa, the perennial ryegrass showed higher tolerance for AOD slag fertilization. The toxicity of the utilization of AOD slag as mineral fertilizer for perennial ryegrass planting is slight. Health risks induced by the consumption of the alfalfa grown on the soil with high AOD slag rates (≥8 wt.%) were detected.