A polymer-infiltrated ceramic network (PICN) material has recently been introduced for dental use and evidence is developing regarding the fit accuracy of such crowns with different preparation designs. The aim of this in vitro study was to evaluate the precision of fit of machined monolithic PICN single crowns in comparison to lithium disilicate crowns in terms of marginal gap, internal gap, and absolute marginal discrepancies. A secondary aim was to assess the effect of finish line configuration on the fit accuracy of crowns made from the two materials. Two master metal dies were used to create forty stone dies, with twenty each for the two finish lines, shoulder and chamfer. The stone dies were scanned to produce virtual models, on which ceramic crowns were designed and milled, with ten each for the four material–finish line combinations (n = 10). Marginal gaps and absolute marginal discrepancies were evaluated at six pre-determined margin locations, and the internal gap was measured at 60 designated points using a stereomicroscope-based digital image analysis system. The influence of the material and finish line on the marginal and internal adaptation of crowns was assessed by analyzing the data using two-way analysis of variance (ANOVA), non-parametric, and Bonferroni multiple comparison post-hoc tests (α = 0.05). ANOVA revealed that the differences in the marginal gaps and the absolute marginal discrepancies between the two materials were significant (p < 0.05), but that those the finish line effect and the interaction were not significant (p > 0.05). Using the Mann–Whitney U test, the differences in IG for ‘material’ and ‘finish line’ were not found to be significant (p > 0.05). In conclusion, the finish line configuration did not seem to affect the marginal and internal adaptation of PICN and lithium disilicate crowns. The marginal gap of PICN crowns was below the clinically acceptable threshold of 120 µm.

Background: Sterilization is required for any biomedical device intended to be used in contact with the human body. Several studies have reported alterations in the bulk and surface properties of such devices after repeated sterilization cycles. These surface modifications may influence other clinical parameters. Therefore, the aim of this study was to investigate the surface and chemical properties of implant scan bodies (SBs) after consecutive autoclave sterilization procedures. Methods: The objective was to analyze the scan bodies using Fourier transform infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS) for chemical analysis and an optical profilometer to analyze the surface roughness. Results: FTIR spectra depicted the appearance of peak at 1741 and 1100 cm⁻¹ due to the diphenyl ether band disappearance. The XPS spectra showed alterations in the elemental composition after autoclaving and roughness were significantly reduced in PEEK BL and TL SBs. Conclusions: These results indicated that some surface modifications were induced by repeated sterilization cycles.