The aim of the present work is to evaluate the rate and mechanisms of the aerobic biodegradation of biopolymer blends under controlled composting conditions using the CO₂ evolution respirometric method. The biopolymer blends of poly (butylene adipate terephthalate) (PBAT) blended with poly (lactic acid) (PLA), and PBAT blended with poly (butylene succinate) (PBS) by melt extrusion, were tested to evaluate the amount of carbon mineralized under home and industrial composting conditions. The changes in the structural, chemical, thermal and morphological characteristics of the biopolymer blends before and after biodegradation were investigated by FT-IR, DSC, TGA, XRD and SEM. Both blends showed higher degradation rates under industrial composting conditions, when compared to home composting conditions. This was confirmed by FT-IR analysis showing an increase in the intensity of hydroxyl and carbonyl absorption bands. SEM revealed that there was microbial colony formation and disintegration on the surfaces of the biopolymer blends. The obtained results suggest that industrial composting conditions are the most suitable for an enhanced biodegradation of the biopolymer blends viz PBAT–PBS and PBAT–PLA.

Polybutylene adipate-co-terephthalate (PBAT) was used in an effort to improve the properties of polybutylene succinate (PBS). The resultant blend consisting of PBS/PBAT (70/30) was reinforced with lignin at different loadings (5 to 15 wt.%) and zinc (ZnO) nanoparticles (1.5 wt.%). Hot melt extrusion and injection moulding were used to prepare the hybrid composites. The mechanical, thermal, physical, self-cleaning, and antimicrobial properties of the resultant hybrid composites were investigated. The transmission electron microscopy (TEM) results confirmed that ZnO was successfully prepared with average diameters of 80 nm. Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction (XRD) confirmed that there were interactions between the fillers and the blend. The tensile strength and elongation at the break of the resultant materials decreased with increasing the loadings, while the tensile modulus showed the opposite trend. The melting behaviour of the blend was practically unaffected by incorporating lignin and ZnO nanoparticles. In addition, the incorporation of fillers reduced the thermal stability of the materials. Furthermore, the incorporation of ZnO nanoparticles introduced photocatalytic properties into the polymer blend, rendering it to be a functional self-cleaning material and enhancing its antimicrobial activities.