Despite progress in small scale electrocatalytic production of hydrogen peroxide (H₂O₂) using a rotating ring-disk electrode, further work is needed to develop a non-toxic, selective, and stable O₂-to-H₂O₂ electrocatalyst for realizing continuous on-site production of neutral hydrogen peroxide. We report ultrasmall and monodisperse colloidal PtP₂ nanocrystals that achieve H₂O₂ production at near zero-overpotential with near unity H₂O₂ selectivity at 0.27 V vs. RHE. Density functional theory calculations indicate that P promotes hydrogenation of OOH* to H₂O₂ by weakening the Pt-OOH* bond and suppressing the dissociative OOH* to O* pathway. Atomic layer deposition of Al₂O₃ prevents NC aggregation and enables application in a polymer electrolyte membrane fuel cell (PEMFC) with a maximum r(H₂O₂) of 2.26 mmol h⁻¹ cm⁻² and a current efficiency of 78.8% even at a high current density of 150 mA cm⁻². Catalyst stability enables an accumulated neutral H₂O₂ concentration in 600 mL of 3.0 wt% (pH = 6.6).

Methane pyrolysis (MP) is a potential technology for CO ₂ -free hydrogen production that generates only solid carbon by-products. However, developing a highly efficient catalyst for stable methane pyrolysis at a moderate temperature has been challenging. We present a new and highly efficient catalyst created by modifying a Ni-Bi liquid alloy with the addition of Mo to produce a ternary NiMo-Bi liquid alloy catalyst (LAC). This catalyst exhibited a considerably low activation energy of 81.2 kilojoules per mole, which enabled MP at temperatures between 450 and 800 Celsius and a hydrogen generation efficiency of 4.05 ml per gram of nickel per minute. At 800 Celsius, the catalyst exhibited 100% H ₂ selectivity and 120 hours of stability.

Layered double hydroxides (LDH) have been extensively investigated for charge storage, however, their development is hampered by the sluggish reaction dynamics. Herein, triggered by mismatching integration of Mn sites, we configured wrinkled Mn/NiCo-LDH with strains and defects, where promoted mass & charge transport behaviors were realized. The well-tailored Mn/NiCo-LDH displays a capacity up to 518 C g⁻¹ (1 A g⁻¹), a remarkable rate performance (78%@100 A g⁻¹) and a long cycle life (without capacity decay after 10,000 cycles). We clarified that the moderate electron transfer between the released Mn species and Co²⁺ serves as the pre-step, while the compressive strain induces structural deformation with promoted reaction dynamics. Theoretical and operando investigations further demonstrate that the Mn sites boost ion adsorption/transport and electron transfer, and the Mn-induced effect remains active after multiple charge/discharge processes. This contribution provides some insights for controllable structure design and modulation toward high-efficient energy storage.