Color is an important indicator for evaluating the quality of natural rubber (NR). Light-colored standard rubbers are widely used in high-grade products and have high economic value. This paper first introduces the history and test standards of the standard light-colored rubber. The origin of color deepening in NR processing, color substances, and its biosynthetic pathway are reviewed. Then, the discoloration mechanism of NR is studied from the perspectives of enzymatic browning (caused by polyphenol oxidase and polyphenols) and non-enzymatic browning (including Maillard reaction and lipid oxidation). Finally, the strategies to control the discoloration of NR will be described.

Natural rubber (NR) gloves manufactured from NR latex are widely utilized in various applications as a personal protective device due to their exceptional barrier characteristics in infection control. However, the use of NR gloves was associated with concerns on NR protein allergy. With comprehensive leaching procedures now a common practice in NR latex glove factories to eliminate latent rubber proteins and chemical allergens, occurrences and complaints of protein allergy from medical glove users have decreased drastically over the past two decades. The present work aims to eliminate further the residual rubber allergens in NR latex through effective purification of the NR latex and compounding the thus purified latex with an established formulation for allergy-free NR for glove applications. NR latex was purified by deproteinization and saponification, respectively. Several analytical techniques were used to verify rubber allergens eliminated in the purified latexes. Saponified NR (SPNR) latex was the purified NR latex of choice since it is devoid of allergenic proteins and poses the lowest risk of Type I allergy. The purified NR latex was compounded with zinc diethyldithiocarbamate (ZDEC), zinc dibutyldithiocarbamate (ZDBC), and zinc 2-mercaptobenzothiazole (ZMBT), respectively, for glove dipping. Among the investigated accelerators, only ZDBC was not detected in the artificial sweat that came into contact with the dipped articles. Thus, it is deduced that ZDBC poses the lowest risk of Type IV allergy to consumers. Additionally, the morphological and physical properties of dipped articles were assessed. It was revealed that the dipped film from the SPNR latex compounded with ZDBC provided thinner and less yellow products with a more uniform internal structure and a tensile strength comparable to those of commercial NR gloves.

Natural rubber (NR) latex contains many components, especially non‐rubber components, which can affect the color of products made from it. There is a growing demand in NR products which are lightly colored or color filled. One way to reduce the yellow color of NR is to remove non‐rubber components, for example, lipids and proteins, from NR. This study focused on several NR latex decoloration techniques, including controlling centrifugation speed and time as well as percentage of total solid content (% TSC) of field latex. It was found that the best condition to reduce yellow color was centrifugation of the field latex containing less than 35% TSC at 12,000 rpm for 30 min. In addition, decoloration of NR latex was very effective by washing the centrifuged latex at least twice. Other factors, such as storage time and drying conditions, promoted coloration of NR due to the oxidation of the non‐rubbers.