With the increasing interest in hydrogen energy, the stability of hydrogen storage facilities and components is emphasized. In this study, we analyzed the effect of high-pressure hydrogen gas treatment in silica-filled EPDM composites with different silica contents. In detail, cure characteristics, crosslink density, mechanical properties, and hydrogen permeation properties were investigated. Results showed that material volume, remaining hydrogen content, and mechanical properties were changed after 96.3 MPa hydrogen gas exposure. With an increase in the silica content, the crosslink density and mechanical properties increased, but hydrogen permeability was decreased. After treatment, high-silica-content composites showed lower volume change than low-silica-content composites. The crack damage due to the decompression caused a decrease in mechanical properties, but high silica content can inhibit the reduction in mechanical properties. In particular, EPDM/silica composites with a silica content of above 60 phr exhibited excellent resistance to hydrogen gas, as no change in their physical and mechanical properties was observed.

This study investigated the synergistic effect of carbon black/multi-wall carbon nanotube (CB/MWCNT) hybrid fillers on the physical and mechanical properties of Ethylene propylene diene rubber (EPDM) composites after exposure to high-pressure hydrogen gas. The EPDM/CB/CNT hybrid composites were prepared by using the EPDM/MWCNT master batch (MB) with 10 phr CNTs to enhance the dispersion of CNTs in hybrid composites. The investigation included a detailed analysis of cure characteristics, crosslink density, Payne effect, mechanical properties, and hydrogen permeation properties. After exposure to 96.3 MPa hydrogen gas, the hydrogen uptake and the change in volume and mechanical properties of the composites were assessed. We found that as the MWCNT volume fraction in fillers increased, the crosslink density, filler–filler interaction, and modulus of hybrid composites increased. The hydrogen uptake and the solubility of the composites decreased with an increasing MWCNT volume fraction in fillers. Moreover, after exposure to hydrogen gas, the change in volume and mechanical properties exhibited a diminishing trend with a higher MWCNT volume fraction. We conclude that the hybridization of CB and CNTs formed strong filler–filler networks in hybrid composites, consequently reinforcing the EPDM composites and enhancing the barrier properties of hydrogen gas.