We investigate systematically the influence of the nature of thiol-type capping ligands on the optical and structural properties of highly luminescent CdTe quantum dots synthesized in aqueous media, comparing mercaptopropionic acid (MPA), thioglycolic acid (TGA), 1-thioglycerol (TGH), and glutathione (GSH). The growth rate, size distribution, and quantum yield strongly depend on the type of surface ligand used. While TGH binds too strongly to the nanocrystal surface inhibiting growth, the use of GSH results in the fastest growth kinetics. TGA and MPA show intermediate growth kinetics, but MPA yields a much lower initial size distribution than TGA. The obtained fluorescence quantum yields range from 38% to 73%. XPS studies unambiguously put into evidence the formation of a CdS shell on the CdTe core due to the thermal decomposition of the capping ligands. This shell is thicker when GSH is used as ligand, as compared with TGA ligands.

Lead halide perovskites have emerged as promising materials for light-emitting devices. Here, we report the preparation of colloidal CsPbBr₃ nanoplatelets (3 × 4 × 23 nm³) experiencing a strong quasi-one-dimensional quantum confinement. Ultrafast transient absorption and broadband fluorescence up-conversion spectroscopies were employed to scrutinize the carrier and quasiparticle dynamics and to obtain a full description of the spectroscopic properties of the material. An exciton binding energy of 350 meV, an absorption cross section at 3.2 eV of 5.0 ± 0.3 × 10^–15 cm^–2, an efficient biexciton Auger recombination lifetime of 9 ± 1 ps, and a biexciton binding energy of 74 ± 4 meV were determined. Moreover, a short-lived emission from hot excitons was observed, which is related to the formation of band-edge excitons. The time constant of both processes is 300 ± 50 fs. These results show that CsPbBr₃ nanoplatelets are indeed quite promising for light-emitting technological applications.