Background: Biodegradable polyurethanes have found widespread use in soft tissue engineering due to their suitable mechanical properties and biocompatibility. Methods: In this study, polyurethane samples were synthesized from polycaprolactone, hexamethylene diisocyanate, and a copolymer of 1,4-butanediol as a chain extender. Polyurethane scaffolds were fabricated by a combination of liquid–liquid phase separation and salt leaching techniques. The effect of the NCO:OH ratio on porosity content and pore morphology was investigated. Results: Scanning electron micrographs demonstrated that the scaffolds had a regular distribution of interconnected pores, with pore diameters of 50–300 µm, and porosities of 64%–83%. It was observed that, by increasing the NCO:OH ratio, the average pore size, compressive strength, and compressive modulus increased. L929 fibroblast and chondrocytes were cultured on the scaffolds, and all samples exhibited suitable cell attachment and growth, with a high level of biocompatibility. Conclusion: These biodegradable polyurethane scaffolds demonstrate potential for soft tissue engineering applications.

In this study, new nano-fluor-hydroxyapatite (nFHA)/polyurethane composite scaffolds were fabricated for potential use in bone tissue engineering. Polyester urethane samples were synthesized from polycaprolactone, hexamethylene diisocyanate, and 1,4-butanediol as chain extender. Nano fluor-hydroxyapatite (nFHA) was successfully synthesized by sol-gel method. The solid–liquid phase separation and solvent sublimation methods were used for preparation of the porous composites. Mechanical properties, chemical structure, and morphological characteristics of the samples were investigated by compressive test, Fourier transform infrared, and scanning electron microscopy (SEM) techniques, respectively. The effect of nFHA powder content on porosity and pore morphology was investigated. SEM images demonstrated that the scaffolds were constituted of interconnected and homogeneously distributed pores. The pore size of the scaffolds was in the range 50–250 µm. The result obtained in this research revealed that the porosity and pore average size decreased and compressive modulus increased with nFHA percentage. Considering morphological, physical, and mechanical properties, the scaffold with a higher ratio of nFHA has suitable potential use in tissue regeneration.

Severe cutaneous injuries may not heal spontaneously and may necessitate the use of supplementary therapeutic methods. Electrospun nanofibers possess high porosity and specific surface area, which provide the necessary microenvironment for wound healing. Here in, the nanofibers of Soluplus-soy protein isolate (Sol-SPI) containing mupirocin (Mp) were fabricated via electrospinning for wound treatment. The fabricated nanofibers exhibited water absorption capacities of about 300.83 ± 29.72% and water vapor permeability values of about 821.8 ± 49.12 g/m² day. The Sol/SPI/Mp nanofibers showed an in vitro degradability of 33.73 ± 3.55% after 5 days. The ultimate tensile strength, elastic modulus, and elongation of the Sol/SPI/Mp nanofibers were measured as 3.61 ± 0.29 MPa, 39.15 ± 5.08 MPa, and 59.11 ± 1.94%, respectively. Additionally, 85.90 ± 6.02% of Mp loaded in the nanofibers was released in 5 days in vitro, and by applying the Mp-loaded nanofibers, 93.06 ± 5.40% and 90.40 ± 5.66% of S. aureus and E. coli bacteria were killed, respectively. Human keratinocyte cells (HaCat) demonstrated notable biocompatibility with the prepared nanofibers. Furthermore, compare to other groups, Sol-SPI-Mp nanofibers caused the fastest re-epithelialization and wound healing in a rat model. The findings of this study present a novel nanofiber-based wound dressing that accelerates the healing of severe skin wounds with the risk of infection.