CoFe₂O₄/graphene oxide hybrids have been successfully fabricated via a facile one-pot polyol route, followed by chemical conversion into FeCo/graphene hybrids under H₂/NH₃ atomosphere.

Dynamic reconstruction of metal sulphides during electrocatalytic oxygen evolution reaction (OER) has hampered the acquisition of legible evidence for comprehensively understanding the phase-transition mechanism and electrocatalytic activity origin. Herein, modelling on a series of cobalt-nickel bimetallic sulphides, we for the first time establish an explicit and comprehensive picture of their dynamic phase evaluation pathway at the pre-catalytic stage before OER process. By utilizing the in-situ electrochemical transmission electron microscopy and electron energy loss spectroscopy, the lattice sulphur atoms of (NiCo)S_1.33particles are revealed to be partially substituted by oxygen from electrolyte to form a lattice oxygen-sulphur coexisting shell surface before the generation of reconstituted active species. Such S-O exchange process is benefitted from the subtle modulation of metal-sulphur coordination form caused by the specific Ni and Co occupation. This unique oxygen-substitution behaviour produces an (NiCo)O_xS_1.33-xsurface to reduce the energy barrier of surface reconstruction for converting sulphides into active oxy/hydroxide derivative, therefore significantly increasing the proportion of lattice oxygen-mediated mechanism compared to the pure sulphide surface. We anticipate this direct observation can provide an explicit picture of catalysts’ structural and compositional evolution during the electrocatalytic process.

The regulation of mechanism on the electrocatalysis process with multiple reaction pathways is more efficient and essential than conventional material engineering for the enhancement of catalyst performance. Here, by using oxygen evolution reaction (OER) as a model, which has an adsorbate evolution mechanism (AEM) and a lattice oxygen oxidation mechanism (LOM), we demonstrate a general strategy for steering the two mechanisms on various La _x Sr _{1− x} CoO _3−δ . By delicately controlling the oxygen defect contents, the dominant OER mechanism on La _x Sr _{1− x} CoO _3−δ can be arbitrarily transformed between AEM-LOM-AEM accompanied by a volcano-type activity variation trend. Experimental and computational evidence explicitly reveal that the phenomenon is due to the fact that the increased oxygen defects alter the lattice oxygen activity with a volcano-type trend and preserve the Co ⁰ state for preferably OER. Therefore, we achieve the co-optimization between the activity and stability of catalysts by altering the mechanism rather than a specific design of catalysts.