The current research focuses on the green synthesis of silver nanoparticles (AgNPs) using a polar extract of taro corms and the evaluation of its antioxidant properties and wound-healing applications. Taro corm extract (100 mL) was treated with a 5 mM AgNO₃ solution (100 mL) at room temperature for the formation of AgNPs, and a color change was observed. The surface plasmon resonance (SPR) peaks in their UV-visible spectra appeared at a range of 438-445 nm. Fourier transform infrared, scanning electron microscopy, energy-dispersive X-ray, dynamic light scattering, and X-ray diffraction were used for the characterization of the taro corms extract-mediated AgNPs (TCE-AgNPs). The synthesized AgNPs were crystalline and spherical, with an average size of 244.9-272.2 nm with a polydispersity index of 0.530 and zeta potential of -18.8 mV, respectively. The antibacterial potential of TCE-AgNPs was tested, and the inhibition zones detected against Cronobacter sakazakii, Pseudomonas aeruginosa, Listeria monocytogenes, and Enterococcus faecalis were 28, 26, 18, and 13 mm, respectively. Furthermore, the antioxidant activity of TCE-AgNPs showed significant radical-scavenging activity compared to the standard used. Collagen content data collected from regenerated tissue and higher collagen content indicated rapid wound healing compared to others, which was seen in a group treated with TCE-AgNP film bandages.

The pH-sensitive polymeric matrix of basil seed gum (BSG), with two different monomers, such as acrylic acid (AA) and N, N-Methylene-bis-acrylamide (MBA), was selected to use in hydrogels preparation through a free radical copolymerization technique using potassium per sulfate (KPS) as a cross linker. BSG, AA and MBA were used in multiple ratios to investigate the polymer, monomer and initiator effects on swelling properties and release pattern of captopril. Characterization of formulated hydrogels was done by FTIR, DSC/TGA, XRD and SEM techniques to confirm the stability. The hydrogels were subjected to a variety of tests, including dynamic swelling investigations, drug loading, in vitro drug release, sol–gel analyses and rheological studies. FTIR analysis confirmed that after the polymeric reaction of BSG with the AA monomer, AA chains grafted onto the backbone of BSG. The SEM micrographs illustrated an irregular, rough, and porous form of surface. Gel content was increased by increasing the contents of polymeric gum (BSG) with monomers (AA and MBA). Acidic and basic pH effects highlighted the difference between the swelling properties with BSG and AA on increasing concentration. Kinetic modelling suggested that Korsmeyer Peppas model release pattern was followed by the drug with the non-Fickian diffusion mechanism.