Within this research the effect of injection molding temperature on polypropylene (PP)/poly(ethylene terephthalate) (PET) blends and microfibrillar composites was investigated. Injection molding blends (IMBs) and microfibrillar composites (MFCs) of PP/PET have been prepared in a weight ratio 70/30. The samples were processed at three different injection molding temperatures (T_im) (210, 230, 280 °C) and subjected to extensive characterization. The observations from the fracture surfaces of MFCs showed that PET fibers can be achieved by three step processing. The results indicated that T_im has a big influence on morphology of IMBs and MFCs. With increasing the T_im, distinctive variations in particle and fiber diameters were noticed. The differences in mechanical performances were obtained by flexural and impact tests. Establishing relationships between the processing parameters, properties, and morphology of composites is of key importance for the valorization of MFC polymers.

Manganese-doped cadmium sulfide (CdS:Mn) nanoparticles were prepared by chemical synthesis using sodium-alginate as template. The preparation of the nanocomposites involved ionic crosslinking of the biopolymer by dimerization of its α-L-guluronic monomers with Cd²⁺ and subsequent formation of the semiconductor nanoparticles upon addition of sulfide ions in the presence of Mn²⁺. The crystalline phase of CdS in the material was confirmed by XRD. The surface morphology of the nanocomposites was investigated by SEM. The observation by TEM showed that the CdS:Mn particles were spherical in shape with diameters of approximately 4 nm. EPR measurements of the CdS:Mn-alginate nanocomposite showed that the Mn²⁺ ions were incorporated in cationic sites of CdS with lower symmetry. Due to a distorted crystal field induced by the Mn²⁺ ions, photoluminescence spectra of the CdS:Mn-alginate showed red fluorescence between 650 nm and 750 nm falling into the optical window for bioimaging in which the light has its maximum tissue penetration depth. It was demonstrated that the interaction between the nanoparticles and the matrix prevents release of CdS into the environment, leading to low acute toxicity of the nanocomposites.

The main goal of this research is to study the development of crystalline morphology and compare it to various mechanical properties of microfibrillar composites (MFCs) based on polypropylene (PP) and poly(ethylene terephthalate) (PET), by adding a functional compatibilizer and a non-functional rubber in two different steps in the processing sequence. The MFCs were prepared at a weight ratio of 80/20 PP/PET by twin screw extrusion followed by cold drawing and injection moulding. The non-functionalized polyolefin-based elastomer (POE) and the functional compatibilizer (i.e., POE grafted with maleic anhydride (POE-g-MA)) were added in a fixed weight percentage at two stages: during extrusion or during injection moulding. The morphology observations showed differences in crystalline structure, and the PP spherulite size was reduced in all MFCs due to the presence of PET fibrils. Their relationship with the mechanical performances of the composite was studied by tensile and impact tests. Adding the functional compatibilizer during extrusions showed better mechanical properties compared to MFCs. Overall, a clear relationship was identified between processing, structure and properties.

In situ microfibrillation and multiflow vibrate injection molding (MFVIM) technologies were combined to control the phase morphology of blended polypropylene (PP) and poly(ethylene terephthalate) (PET), wherein PP is the majority phase. Four kinds of phase structures were formed using different processing methods. As the PET content changes, the best choice of phase structure also changes. When the PP matrix is unoriented, oriented microfibrillar PET can increase the mechanical properties at an appropriate PET content. However, if the PP matrix is an oriented structure (shish-kebab), only the use of unoriented spherical PET can significantly improve the impact strength. Besides this, the compatibilizer polyolefin grafted maleic anhydride (POE-g-MA) can cover the PET in either spherical or microfibrillar shape to form a core–shell structure, which tends to improve both the yield and impact strength. We focused on the influence of all composing aspects—fibrillation of the dispersed PET, PP matrix crystalline morphology, and compatibilized interface—on the mechanical properties of PP/PET blends as well as potential synergies between these components. Overall, we provided a theoretical basis for the mechanical recycling of immiscible blends.

Several mixed recycled plastics, namely, mixed bilayer polypropylene/poly (ethylene terephthalate) (PP/PET) film, mixed polyolefins (MPO) and talc-filled PP were selected for this study and used as matrices for the preparation of microfibrillar composites (MFCs) with PET as reinforcement fibres. MFCs with recycled matrices were successfully prepared by a three-step processing (extrusion—cold drawing—injection moulding), although significant difficulties in processing were observed. Contrary to previous results with virgin PP, no outstanding mechanical properties were achieved; they showed little or almost no improvement compared to the properties of unreinforced recycled plastics. SEM characterisation showed a high level of PET fibre coalescence present in the MFC made from recycled PP/PET film, while in the other MFCs, a large heterogeneity of the microstructure was identified. Despite these disappointing results, the MFC concept remains an interesting approach for the upcycling of mixed polymer waste. However, the current study shows that the approach requires further in-depth investigations which consider various factors such as viscosity, heterogeneity, the presence of different additives and levels of degradation.