The present work contributes an engineered life cycle assessment (LCA) of hydrogen fuel cell passenger vehicles based on a real-world driving cycle for semi-urban driving conditions. A new customized LCA tool is developed for the comparison of conventional gasoline and hydrogen fuel cell vehicles (FCVs), which utilizes a dynamic vehicle simulation approach to calculate realistic, fundamental science based fuel economy data from actual drive cycles, vehicle specifications, road grade, engine performance, fuel cell degradation effects, and regenerative braking. The total greenhouse gas (GHG) emission and life cycle cost of the vehicles are compared for the case of hydrogen production by electrolysis in British Columbia, Canada. A 72% reduction in total GHG emission is obtained for switching from gasoline vehicles to FCVs. While fuel cell performance degradation causes 7% and 3% increases in lifetime fuel consumption and GHG emission, respectively, regenerative braking improves the fuel economy by 23% and reduces the total GHG emission by 10%. The cost assessment results indicate that the current FCV technology is approximately $2,100 more costly than the equivalent gasoline vehicle based on the total lifetime cost including purchase and fuel cost. However, prospective enhancements in fuel cell durability could potentially reduce the FCV lifetime cost below that of gasoline vehicles. Overall, the present results indicate that fuel cell vehicles are becoming both technologically and economically viable compared with incumbent vehicles, and provide a realistic option for deep reductions in emissions from transportation. Copyright © 2016 John Wiley & Sons, Ltd.

Lifetime-limiting failure of fuel cell membranes is generally attributed to their chemical and/or mechanical degradation. Although both of these degradation modes occur concurrently during operational duty cycles, their uncoupled investigations can provide useful insights into their individual characteristics and consequential impacts on the overall membrane failure. X-ray computed tomography is emerging as an advantageous tool for fuel cell failure analysis due to its non-destructive and non-invasive 3D imaging capabilities at ambient conditions. In the present work, post-mortem failure analysis of pure mechanical and pure chemical membrane degradation modes is performed three-dimensionally using this technique. A uniquely comprehensive analysis afforded by this technique reveals that membrane failure is almost exclusively characterized by crack formations during mechanical degradation and by severe thinning accompanied by electrode shorting and pinhole formation during chemical degradation, respectively. Catalyst layer cracks, particularly on the cathode side, are found to interact strongly with mechanically induced membrane cracks. The conjoint effect of chemical and mechanical stressors is established as a necessary requirement for: (i) exclusive membrane crack development independent of catalyst layer cracks; and (ii) crack branching during membrane crack propagation. Overall, the membrane failure analysis improves its reliability and quantitative character with the adoption of 3D imaging.