This study analyzes the optimal seasonal ambient temperature during welding and welding speed conditions for securing high tensile strength of ethylene vinyl acetate (EVA) waterproofing sheets bonded for roofing, installed by hot air welded joints (overlaps). Seven separate ambient temperature conditions (−10, −5, and 0 °C for winter conditions, 20 °C for the normal condition, and 25, 30, and 35 °C for summer conditions) were set for the test variable and seven speed conditions (3, 4, 5, 6, 7, 8, and 9 m/min) for hot air welding. Based on these conditions, EVA sheet joint specimens were prepared, and the tensile strength of the joint sections was tested and measured. Tensile strength results, compared to normal temperature conditions (20 °C) showed an increase in the summer temperature condition but a decrease during winter temperature conditions. The analysis on the effects of the welding speed showed that in summer temperature conditions (25, 30, and 35 °C), the optimum hot air welding speed is 4.3~9.0 m/min at 25 °C, 4.7~8.7 m/min at 30 °C and 5.2~8.6 m/min at 35 °C, whereas in winter (−10, −5, and 0 °C), the optimum hot air welding temperature is 3~4.1 m/min at −10 °C, 3~4.6 m/min at −5 °C and 3~4.9 m/min at 0 °C. Research results demonstrate that it is imperative to consider the welding speed in accordance to the respective seasonal temperature conditions to secure construction quality of the EVA joints for roofing.

Polyurethanes with water expansion properties are manufactured by incorporating polyurethane resins and superabsorbent polymers. This study aimed to present an optimal mixing ratio of a superabsorbent polymer that can express the effective waterproofing performance of a polyurethane material with water expansion properties. The evaluation results confirmed that the waterproofing performance was exerted at a superabsorbent polymer mixing ratio of more than 10% and an expansion ratio of 150% or more, which were then set as the minimum standard value for ensuring waterproofing performance. In addition, chemical erosion (by hydrochloric acid, sulfuric acid, nitric acid, alkali, and sodium chloride), freeze-thaw, and wet-dry cycles were set as deterioration conditions to determine the optimal mixing ratio for the superabsorbent polymer under conditions of use, and the maximum expansion ratio was evaluated after pretreatment under the deterioration conditions. It was found that, based on the minimum standard value for the waterproofing performance set above, the superabsorbent polymer mixing ratio that can ensure an expansion ratio of 150% or more under all deterioration conditions was 14%.

Sheet-coated composite waterproofing (SCCW) have been developed to overcome the natural weakness of singly-ply coating or sheet waterproofing systems for roofing, but there are currently multiple types of SCCW joints. Conventional standard tensile strength testing results show that all SCCW joint types seem to pass the minimum requirement and current selection of SCCW type is dictated on the principle of ‘higher tensile strength is better’, but it has not been experimentally studied as to which type is the optimal to respond to environmental degradation while under the effect of zero-span tensile stress occurring during concrete joint displacement. In this study, five types of SCCW joints were tested: Overlap Bond (OB) type, Overlap Heated-Air Welding (OH) type, Butt Joint I Type (BI), Butt Joint T Type (BT), and Butt Joint Separation Movement Type (BS). These types of joint designs were subjected to Alkali, NaCl, and H₂SO₄ exposure, and temperature change (60 °C and −20 °C) for determining changes to tensile strength in the joint section. Tensile strength change results are compared to joint displacement resistance test results of specimens that were treated with chemical and temperature degradation. With the exception of chemical exposure conditioning, the Overlap type joints generally had higher tensile strength compared to the butt joint types, but joint displacement test results showed the opposite results, suggesting that complex joints found in SCCW require new evaluation method for quality assessment.

A revised oil leakage evaluation regime is proposed in response to the oil leakage problems of emulsion-based non-curable synthetic polymer rubberized gel (ENC-SPRG) used as a waterproofing material in concrete slabs of residential underground structures. Oil leakage from ENC-SPRG can cause significant economic and environmental damage. As ENC-SPRG waterproofing material is relatively new in the global waterproofing market, a systematic quality control for ENC-SPRG products being manufactured and exported globally is currently non-existent. For the selection of optimal ENC-SPRG, six assessment parameters comprised of averaged and daily average oil leakage mass, averaged and daily average filler content settlement, oil leakage area, and oil leakage duration are proposed. Five ENC-SPRG product specimens are tested to obtain the property values of each parameter. The property values derived from the test results are compared between the tested ENC-SPRG product specimens. With the demonstration of this evaluation regime, a quantified method for a comparative assessment of ENC-SPRG type waterproofing materials is established.

This study seeks to analyze how the degree of carbonation and the application of waterproofing and anticorrosive materials affect carbonation in water reservoirs among the water treatment facilities managed by the Seoul Metropolitan Government. To guarantee similarity of the experimental group, 42 highly similar water reservoirs were selected from among the water supply reservoirs currently in operation in Seoul. On-site carbonation assessments were performed in order to derive the carbonation rate coefficients. In the water reservoirs with applied waterproofing and anticorrosive materials immediately after public service, the upper and lower limits were D = 1.13$\sqrt{\mathrm{t}}$ and D = 0.29$\sqrt{\mathrm{t}}$, respectively, whereas those of the water reservoir applied with waterproofing and anticorrosive materials after 15 years of service life were D = 1.89$\sqrt{\mathrm{t}}$ and D = 0.94$\sqrt{\mathrm{t}}$, respectively. The comparative analysis showed that the rate of reduction in the carbonation rate was about 10.4% to 16.8% in the water reservoirs applied with waterproofing and anticorrosive methods after 15 years of service life. However, reduction in the carbonation rate was about 46.4% to 74.3% in the water reservoirs applied with waterproofing and anticorrosive methods at the initial stage of service life. It was confirmed that the early application of waterproofing and anticorrosive materials is effective in suppressing carbonation of concrete water reservoir structures.