The synthesis of lightweight yet strong-ductile materials has been an imperative challenge in alloy design. In this study, the CoCrNi-based medium-entropy alloys (MEAs) with added Al and Si were manufactured by vacuum arc melting furnace subsequently followed by cool rolling and anneal process. The mechanical responses of CoCrNiAl_0.1Si_0.1 MEAs under quasi-static (1 × 10⁻³ s⁻¹) tensile strength showed that MEAs had an outstanding balance of yield strength, ultimate tensile strength, and elongation. The yield strength, ultimate tensile strength, and elongation were increased from 480 MPa, 900 MPa, and 58% at 298 K to 700 MPa, 1250 MPa, and 72% at 77 K, respectively. Temperature dependencies of the yield strength and strain hardening were investigated to understand the excellent mechanical performance, considering the contribution of lattice distortions, deformation twins, and microbands. Severe lattice distortions were determined to play a predominant role in the temperature-dependent yield stress. The Peierls barrier height increased with decreasing temperature, owing to thermal vibrations causing the effective width of a dislocation core to decrease. Through the thermodynamic formula, the stacking fault energies were calculated to be 14.12 mJ/m² and 8.32 mJ/m² at 298 K and 77 K, respectively. In conclusion, the enhanced strength and ductility at cryogenic temperature can be attributed to multiple deformation mechanisms including dislocations, extensive deformation twins, and microbands. The synergistic effect of multiple deformation mechanisms lead to the outstanding mechanical properties of the alloy at room and cryogenic temperature.

Here, we investigate structure and mechanical change of Cu and Al current collector during cycling and analyze the contribution to capacity attenuation of Sb-based lithium-ion batteries (LIBs). There exists migration of C, Sb, and Li atoms to the inside of Cu current collector, and diffusion of Li, Co, and O atoms to the inside of Al current collector during cycling, which results in the formation of a porous film of Li₂SbCu (with the thickness of 21 µm after 100 cycles) and a relatively dense film of Al₂O₃ (with the thickness of 23 µm after 100 cycles) on the surface of Cu and Al current collector, respectively. The formation of films results in a weak bond between active layer and current collector, and the increase of hardness of 0.84 GPa and modulus of 22.5 GPa for Cu current collector after 100 cycles, which is adverse to the charge capacity and cycling stability. Nevertheless, Al₂O₃ films caused hardness decrease of 0.53 GPa and modulus decrease of 18.93 GPa of Al current collector after 100 cycles, which contributes to the improvement of cycling stability and charge capacity. This study provides an understanding of the capacity loss of Sb-based LIBs from the perspective of structural degradation of current collectors.

A FeNx-C-based catalyst is considered one of the most promising candidates for the highest oxygen reduction reaction (ORR) activities among nonprecious metal-based electrocatalysts. In this work, a unique catalyst of nitrogen-doped twisted macroscopic graphene tubes decorated with Fe-Nx and bamboo-like carbon nanotubes (CNT) was prepared by using twisted iron wire as a template and cyanamide as a carbon source. The microstructure and physicochemical natures of the samples were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopic (XPS), X-ray diffraction (XRD), and nitrogen adsorption/desorption measurements. Torsion can promote the dislocation of the iron wire lattice, and activate the surface Fe atoms, thus leading to the growth of bamboo-like carbon nanotubes and forming iron nitride. The product has a graphene-like macroscopic tube structure and exhibits excellent ORR activity. Such excellent ORR performance may be ascribed to the synergistic effect, including high ORR catalytic sites caused by the dislocation of the iron wire lattice, nitrogen heteroatoms doping, favorable reactant transport channels provided by macroscopic tube structure, and fast electron transfer rate induced by 3D continuous networks.