This study investigated the effects of microwave sintering on the microstructures and properties of copper-rGO composites. Graphene oxide was coated onto copper particles by wet ball milling, and copper-rGO composites were formed upon microwave sintering in an argon atmosphere. Scanning electron microscopy was then used to observe the mixing in the ball-milled composite powder, and the morphology of the bulk composite after microwave sintering. Raman spectra revealed how graphene oxide changed with ball milling and with microwave sintering. The microhardness, electrical conductivity, and thermal conductivity of the composite were also measured. The results showed that graphene oxide and copper particles were well combined and uniformly distributed after wet ball milling. The overall microhardness of microwave-sintered samples was 81.1 HV, which was 14.2% greater than that of pure copper (71 HV). After microwave sintering, the microhardness of the samples in areas showing copper oxide precipitates with eutectic structures was 89.5 HV, whereas the microhardness of the precipitate-free areas was 70.6 HV. The electrical conductivity of the samples was 87.10 IACS%, and their thermal conductivity was 391.62 W·m⁻¹·K⁻¹.

The present work demonstrated the first-ever preparation of block specimens by the microwave sintering of H13 alloy powder. Varying proportions of vanadium powder (1.5%, 2.5%, 3.5%, 4.5%, and 5.5% on a mass basis) were added to H13 mold steel and these mixtures were sintered using microwaves. X-ray fluorescence spectroscopy was employed to determine the compositions of the resulting specimens and vanadium percentages of 1.56%, 2.04%, 3.10%, 4.06%, and 4.20% were determined. These results demonstrate a clear trend, with significantly lower vanadium amounts than expected based on the nominal values at higher vanadium loadings. Different samples were also found to exhibit different degrees of ablation, and this effect was related to the presence of voids in the materials. The surface compositions of these specimens were examined by laser-induced breakdown spectroscopy and were found to be relatively uniform. The microstructures as well as the hardness properties of the materials were assessed. Microwave sintering of 100 g specimens at 1300 °C for 10-min generated samples with hardness values ranging from 205 HV (at the lowest vanadium content) to 175.2 HV (at the highest vanadium content). The wear behavior of samples prepared by microwave sintering H13 die steel with different vanadium contents at room temperature has been studied. The results showed that 1.5% vanadium content is the best mass ratio.