In this study, as a measure to enhance the antimicrobial activity of biomaterials, the selenium ions have been substituted into hydroxyapatite (HA) at different concentration levels. To balance the potential cytotoxic effects of selenite ions (SeO₃²⁻) in HA, strontium (Sr²⁺) was co-substituted at the same concentration. Selenium and strontium-substituted hydroxyapatites (Se-Sr-HA) at equal molar ratios of x Se/(Se + P) and x Sr/(Sr + Ca) at (x = 0, 0.01, 0.03, 0.05, 0.1, and 0.2) were synthesized via the wet precipitation route and sintered at 900 °C. The effect of the two-ion concentration on morphology, surface charge, composition, antibacterial ability, and cell viability were studied. X-ray diffraction verified the phase purity and confirmed the substitution of selenium and strontium ions. Acellular in vitro bioactivity tests revealed that Se-Sr-HA was highly bioactive compared to pure HA. Se-Sr-HA samples showed excellent antibacterial activity against both Gram-negative (Escherichia coli) and Gram-positive (Staphylococcus carnosus) bacterial strains. In vitro cell–material interaction, using human osteosarcoma cells MG-63 studied by WST-8 assay, showed that Se-HA has a cytotoxic effect; however, the co-substitution of strontium in Se-HA offsets the negative impact of selenium and enhanced the biological properties of HA. Hence, the prepared samples are a suitable choice for antibacterial coatings and bone filler applications.

We report here alumina-substituted Keggin tungstoborate/kaolin clay composite materials (KAB/kaolin) as polyethylene cracking catalysts. KAB/kaolin composites with varying concentrations of KAB (10–50 wt.%) were synthesized by the wet impregnation method and successfully characterized by Fourier-transform infrared spectroscopy, powder X-ray diffraction, thermo-gravimetric analysis and scanning electron microscopy with energy dispersive X-ray spectroscopy analytical techniques. Use of KAB loaded kaolin composites as the catalyst for low-density polyethylene (LDPE) cracking exhibited a higher percentage of polymer conversion (99%), producing 84 wt.% of fuel oil and negligible amount (˂ 1 wt.%) of solid residue while thermal cracking produced ~22 wt.% residue. Furthermore, gas chromatography–mass spectrometry analysis of oil obtained by non-catalytic cracking exhibited a high selectivity to high molecular weight hydrocarbons (C₁₃–C₂₃) compared to the catalytic cracking where 70 mol.% of gasoline range hydrocarbons (C₅–C₁₂) were produced. We propose that higher cracking ability of our prepared catalysts might ensue from both Brønsted and Lewis acid sites (from KAB and kaolin respectively), which enhanced the yield of liquid fuel products and reduced the cracking temperature of LDPE. These findings suggest that the prepared composites were cost-effective and excellent cracking catalysts that could be recommended for highly efficient conversion of waste plastic materials to petrochemicals at an industrial scale.