In this work, hierarchically porous composites were prepared in the form of activated carbon cloth (CC) Busofit T–1–055 filled with an electrically conductive polymer, polyaniline (PANI), for use as pseudocapacitive electrodes of electrochemical supercapacitors (SCs). CC fibers have high nanoporosity and specific surface area, so it was possible to deposit (via the chemical oxidative polymerization of aniline) a significant amount of PANI on them in the form of a thin layer mainly located on the inner surface of the pores. Such morphology of the composite made allowed the combining of the high capacitive characteristics of PANI with the reversibility of electrochemical processes, high columbic efficiency and cyclic stability rather typical for carbon materials of double-layer SCs. The highest capacitance of composite electrodes of about 4.54 F/cm² with high cyclic stability (no more than 8% of capacity loss after 2000 charge–discharge cycles with a current density of 10 A/cm²) and columbic efficiency (up to 98%) was achieved in 3 M H₂SO₄ electrolyte solution when PANI was synthesized from an aniline hydrochloride solution with a concentration of 0.25 M. Trasatti analysis revealed that 27% of specific capacitance corresponded to pseudocapacitance, and 73% to the double-layer capacitance.

In this paper we study in detail the products formed during the process of water-assisted thermal oxidative decomposition (TOD) of polypropylene in the presence of pressurized oxygen. A set of techniques has shown that the main decomposition product in such a process is acetic acid with small amounts of other carboxylic acids (formic, propionic, succinic). The kinetics of carboxylic acid formation is studied by means of gas chromatography–mass-spectrometry as well as capillary electrophoresis, and the possible mechanisms behind the products formation are discussed. The role of water is considered based on the results obtained from substituting H₂O with D₂O in TOD. Compositions of residual oligomeric fractions as well as gas products are analyzed.