Eight persons from five institutions in different countries carried out polymerizations of aniline following the same preparation protocol. In a "standard" procedure, aniline hydrochloride was oxidized with ammonium peroxydisulfate in aqueous medium at ambient temperature. The yield of polyaniline was higher than 90 % in all cases. The electrical conductivity of polyaniline hydrochloride thus prepared was 4.4 ± 1.7 S cm^-1 (average of 59 samples), measured at room temperature. A product with defined electrical properties could be obtained in various laboratories by following the same synthetic procedure. The influence of reduced reaction temperature and increased acidity of the polymerization medium on polyaniline conductivity were also addressed. The conductivity changes occurring during the storage of polyaniline were monitored. The density of polyaniline hydrochloride was 1.329 g cm^-3. The average conductivity of corresponding polyaniline bases was 1.4 x10­8 S cm^-1, the density being 1.245 g cm^-1. Additional changes in the conductivity take place during storage. Aging is more pronounced in powders than in compressed samples. As far as aging effects are concerned, their assessment is relative. The observed reduction in the conductivity by ~10 % after more than one-year storage is large but, compared with the low conductivity of corresponding polyaniline (PANI) base, such a change is negligible. For most applications, an acceptable level of conductivity may be maintained throughout the expected lifetime.

Polyaniline (PANI), a conducting polymer, was prepared by the oxidation of aniline with ammonium peroxydisulfate in various aqueous media. When the polymerization was carried out in the solution of strong (sulfuric) acid, a granular morphology of PANI was obtained. In the solutions of weak (acetic or succinic) acids or in water, PANI nanotubes were produced. The oxidation of aniline under alkaline conditions yielded aniline oligomers. Fourier transform infrared (FTIR) spectra of the oxidation products differ. A group of participants from 11 institutions in different countries recorded the FTIR spectra of PANI bases prepared from the samples obtained in the solutions of strong and weak acids and in alkaline medium within the framework of an IUPAC project. The aim of the project was to identify the differences in molecular structure of PANI and aniline oligomers and to relate them to supramolecular morphology, viz. the nanotube formation. The assignment of FTIR bands of aniline oxidation products is reported.