Adsorption of carbon dioxide (CO₂), as well as many other kinds of small molecules, is of importance for industrial and sensing applications. Metal-organic framework (MOF)-based adsorbents are spotlighted for such applications. An essential for MOF adsorbent application is a simple and easy fabrication process, preferably from a cheap, sustainable, and environmentally friendly ligand. Herein, we fabricated a novel structural, thermally stable MOF with fluorescence properties, namely Zn [5-oxo-2,3-dihydro-5H-[1,3]-thiazolo [3,2-a]pyridine-3,7-dicarboxylic acid (TPDCA)] • dimethylformamide (DMF) •0.25 H₂O (coded as QUF-001 MOF), in solvothermal conditions by using zinc nitrate as a source of metal ion and TPDCA as a ligand easy accessible from citric acid and cysteine. Single crystal X-ray diffraction analysis and microscopic examination revealed the two-dimensional character of the formed MOF. Upon treatment of QUF-001 with organic solvents (such as methanol, isopropanol, chloroform, dimethylformamide, tetrahydrofuran, hexane), interactions were observed and changes in fluorescence maxima as well as in the powder diffraction patterns were noticed, indicating the inclusion and intercalation of the solvents into the interlamellar space of the crystal structure of QUF-001. Furthermore, CO₂ and CH₄ molecule sorption properties for QUF-001 reached up to 1.6 mmol/g and 8.1 mmol/g, respectively, at 298 K and a pressure of 50 bars.

Cyclohexylammonium hexaisothiocyanatonickelate(II) dihydrate, (C₆H₁₁NH₃)₄[Ni(NCS)₆]·2H₂O, was synthesized, for the first time, by a four-step method in a yield of 95%. The compound was fully characterized by elemental microanalysis, Fourier transform infrared (FTIR), ultraviolet-visible-near infrared (UV-Vis-NIR), and nuclear magnetic resonance (NMR) spectroscopy and thermogravimetry. A single crystal X-ray diffraction (SXRD) gave the monoclinic space group P2₁/c with a = 15.8179 (5) Å, b = 10.6222 (3) Å, c = 13.8751 (4) Å, β = 109.362 (1)°, V = 2199.45 (11) ų, Z = 2 (T = 293 K) for this novel hybrid organic–inorganic compound. The title compound was employed as a single-source precursor for the synthesis of mesoporous, high surface area nickel oxide (53 Å; 452 m²/g) and nickel sulfide (46 Å; 220 m²/g) via pyrolysis under air at 550 °C or helium atmosphere at 500 °C, respectively. X-ray powder diffraction (XRPD) demonstrated the nanocrystalline nature of both NiO and NiS with an average crystallite size of 16 and 54 nm, respectively. Scanning electron microscope (SEM) indicated the formation of agglomerated, quasi-spherical particles of nickel oxide and agglomerated flake-like structures of nickel sulfide. The high surface area, porosity, and nanocrystallinity of both NiO and NiS, obtained via this approach, are promising for a wide spectrum of applications.